Method for preparing powder of nylon
A technology of nylon powder and nylon, which is applied in the chemical industry, can solve the problems of difficult recovery and treatment of aqueous solution, limited application range, difficulty in controlling the ratio of additives and polyamide resin, etc., and achieves the effects of easy implementation, convenient procurement, and good powder fluidity
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0022] Example 1
[0023] Nylon 1212 resin, antioxidant 1010 (chemical name: tetra[β-(3,5-di-tert-butyl 4-hydroxyphenyl) propionic acid] pentaerythritol ester), weight ratio of titanium dioxide to ethanol 93.5:0.5:6: 300, the nozzle diameter of the nozzle is 1mm.
[0024] The process is as follows: the nylon resin, ethanol and additives are respectively added to the high-pressure stirring vessel, stirred and heated, heated to 150°C, and kept at a constant temperature for 30 minutes under stirring. The pressure at this time is about 1 MPa.
[0025] The high-temperature and high-pressure mixture material is pressurized and transported to the pressure spray dryer for spray drying through the insulated pipeline. The spray pressure of the material is 1.8Mpa after pressurization. The power and air volume of the dryer are adjusted to keep the air inlet temperature at 140±5°C. The temperature of the air outlet is maintained at 85±5°C, and nylon powder is collected at the outlet of the dry...
Example Embodiment
[0026] Example 2
[0027] The autoclave was kept at 145°C for 30 minutes. At this time, the pressure was about 0.9 MPa and the others were the same as in Example 1 to obtain nylon powder with an average particle size of 120 μm.
Example Embodiment
[0028] Example 3
[0029] The nozzle diameter of the nozzle is 1.5 mm and the others are the same as in Example 1, to obtain nylon powder with an average particle size of 150 μm.
PUM
Property | Measurement | Unit |
---|---|---|
The average particle size | aaaaa | aaaaa |
Particle size | aaaaa | aaaaa |
Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap