Highly effective antistatic agglomerate for biaxial tension polypropylene and its preparation method

An antistatic masterbatch and biaxial stretching technology, applied in the field of polypropylene polymer modification, can solve the problems of easy aging, redness of film formation, poor film formation, etc. good film effect

Inactive Publication Date: 2006-05-03
SHANGHAI SUNNY
View PDF0 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The antistatic effect of existing BOPP is not long-lasting. After adding an antistatic agent, the film-forming property is poor,

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0033] Example 1

[0034] The special material for biaxially oriented polypropylene BOPP is used as the matrix resin, the antistatic agent is a combination of glyceride and hydroxyethyl alkylamine (1:1), and superfine SiO 2 The particles are grinding agents, stearic acid amide is used as dispersant, 1010 and 168 (1:1) are used as antioxidants, the inhibitor is an amine inhibitor, and 770 is used as an antioxidant.

[0035] raw material name

[0036] Put all the raw materials into a high-mixer and mix for 4 minutes, discharge them, and then extrude and pelletize them with a screw extruder. The processing temperature is 200°C and the screw rotation speed is 450 rpm to prepare BOPP high-efficiency antistatic masterbatch. grain.

Example Embodiment

[0037] Example 2

[0038] Take BOPP as matrix resin, antistatic agent is a combination of saturated partially esterified glyceride and hydroxyethyl alkylamine (1:1), and superfine SiO 2 The particle is a grinding agent, stearic acid amide is used as a dispersant, 1010 and 168 (1:1) are used as an antioxidant, the inhibitor is an amine inhibitor, and a hindered amine light stabilizer 770 / 944 ( 1:1) is an antioxidant.

[0039] raw material name

[0040] With the same processing technology as in Example 1, a high-efficiency antistatic masterbatch for biaxially oriented polypropylene was prepared.

[0041] Film A

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a highly effective antistatic agglomerate for biaxial tension polypropylene and its preparation method, wherein the agglomerate comprises raw materials of the following constituents (by weight proportion): polypropylene 70-90%, antistatic agent 8-30%, grinding agent 0.1-1%, dispersing agent 0.1-2%, anti-oxidant 0.1-1%, inhibiting agent 0.1-0.5%, anti-ageing 0.1-0.5%.

Description

technical field [0001] The invention relates to a high-efficiency antistatic masterbatch for biaxially stretched polypropylene and a preparation method thereof. It has long-term antistatic performance at a relatively low dosage and can be used to manufacture polypropylene film products with antistatic performance. Technical field of propylene polymer modification. technical background [0002] Biaxially oriented polypropylene (BOPP) film has the characteristics of high gloss, high stiffness, good gas barrier properties, and high impact strength. It is a high-transparency packaging material with excellent performance. Since the late 1980s, BOPP films have been widely used in the packaging of food, beverages, cigarettes, clothing and other industries. The antistatic effect of existing BOPP is not long-lasting. After adding antistatic agent, the film-forming properties are poor, the dispersion is not good, there are many defects, and it is easy to age, the film becomes red, an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/12B29C55/00C08K5/524
Inventor 辛敏琦陈晓东杨涛唐倬吴小龙
Owner SHANGHAI SUNNY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap