Picture-grade high-light water-proof colour ink-jet printing paper

A technology of color inkjet and printing paper, applied in the direction of metal coating, specific visual effect coating, etc., can solve the problems of insufficient gloss of the coating, lack of operability, and no in-depth elaboration of the ink receiving layer, etc., to achieve Bright color, good transparency, and realistic color reproduction effect

Inactive Publication Date: 2006-08-09
SHANTOU XINXIE SPECIAL PAPER TECH
View PDF3 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The ink-absorbing layer of the printing photo paper is an alumina material containing a pigment particle size below 150 nanometers. When the particle size of the nano-alumina is large, the gloss of the coating is not enough. How to use does not make a reasonable explanation, so it lacks operability
[0006] Chinese patent CN1558025 discloses "manufacturing method of high-gloss color inkjet photo paper", but this patent does not elaborate deeply on the ink receiving layer

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0064] 1. Formula:

[0065] Raw material weight percentage (wt%)

[0066] Alumina (AL) with a particle size of 30 to 80 nanometers 2 o 3 ) 20g

[0067] Inorganic silica sol with particle size less than 20nm (30% concentration) 8g

[0068] Modified polyamine PloyFIX-700 (strong cationic dispersant) 2g

[0069] Deionized water 70g

[0070] 2. Preparation of coating solution:

[0071] 1. Dilute the cationic dispersant—modified polyamine (PloyFIX-700) with deionized water;

[0072] 2. Add nano-alumina to the diluted modified polyamine solution under high-speed stirring to prepare a modified nano-alumina solution;

[0073] 3. While stirring, add inorganic silica sol to the above-mentioned modified nano-alumina solution to prepare a coating solution.

[0074] 3. Processing conditions of inkjet paper:

[0075] Coating solution concentration: the concentration of the above coating solution is 30%, and the concentration of nano-modified alumina in the coating is 20%;

[0076]...

Embodiment 2

[0088] 1. Formula:

[0089] raw material weight

[0090] Alumina (AL) with a particle size of 30 to 80 nanometers 2 o 3 ) 18g

[0091] Inorganic silica sol (concentration 30%) with particle size less than 20nm 7g

[0092] Modified polyamine PloyFIX-700 (strong cationic dispersant) 1g

[0093] Polyvinyl alcohol 1788 (adhesive) 1g

[0094] Glycerol (plasticizer) 0.7g

[0095] Brightener JB 0.3g

[0096] Melamine formaldehyde resin (waterproofing agent) 0.5g

[0097] Acrylic ester (color fixing agent) 1.5g

[0098] Deionized water 70g

[0099] 2. Preparation of coating solution:

[0100] 1. Dilute the cationic dispersant—modified polyamine (PloyFIX-700) with deionized water;

[0101] 2. Add nano-alumina to the diluted modified polyamine solution under high-speed stirring to prepare a modified nano-alumina solution;

[0102] 3. While stirring, add nano-inorganic silica sol and polyvinyl alcohol (1788) aqueous solution to the above-mentioned modified nano-alumina soluti...

Embodiment 3

[0118] 1. Formula:

[0119] raw material weight

[0120] Alumina (AL) with a particle size of 30 to 80 nanometers 2 o 3 ) 6g

[0121] Inorganic silica sol with particle size less than 20nm (30% concentration) 4g

[0122] Trimethyldodecylammonium chloride (strong cationic dispersant) 1g

[0123] Brightener JB 0.3g

[0124] Amino resin (water repellent) 0.5g

[0125] Acrylic ester (color fixing agent) 1g

[0126] Deionized water 87.2g

[0127] 2. Preparation of coating solution:

[0128] 1. Dilute the cationic dispersant - trimethyl dodecyl ammonium chloride with deionized water;

[0129] 2. Add nano-alumina to the diluted trimethyldodecylammonium chloride solution under high-speed stirring to prepare a modified nano-alumina solution;

[0130] 3. While stirring, add nano-inorganic silica sol to the above-mentioned modified nano-alumina solution;

[0131] 4. Under the condition of high-speed stirring, add whitening agent JB, water-repellent amino resin, and color-fixing ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
specific surface areaaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

Photo-stage high brightness water-proof color ink-jet printing paper includes a basic material and a coat coated on it characterizing that said coat contains nm modified Al2O modified by a strong anode ion dispersing agent and a bonder, since the coat contains modified Al2O with the diameter of 30-80nm and inorganic silicon sol with the diameter smaller than 20nm, the invented paper can either absorb water ink or make the ink not to disperse.

Description

technical field [0001] The invention relates to the technical field of color ink-jet printing paper, more specifically, to a photo-grade high-gloss waterproof color ink-jet printing paper. Background technique [0002] After more than 20 years of hard work by Chinese people, China's printing consumables have become an important part of global printing consumables. With the rapid development of the IT industry, digital cameras, and inkjet printers in society, the downstream supporting materials—color inkjet printing Paper follows closely behind, becoming a product with fast-growing market demand and huge profits, and it is increasing at a rate of more than 25% per year. [0003] Photo-grade high-gloss waterproof color inkjet printing paper worldwide is basically monopolized by multinational companies such as Epson, Kodak, HP, Fuji, etc. However, with the upgrading of products, domestic manufacturers also produce such products, but most manufacturers High-gloss color inkjet p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D21H19/66D21H19/02
Inventor 翟大昌
Owner SHANTOU XINXIE SPECIAL PAPER TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More