A thermal insulation baffle and directional solidification technology, applied in the field of new high-temperature thermal insulation baffles, can solve the problems of heating zone loss, affecting the temperature gradient of the upper and lower zones, complex preparation process, etc., to achieve temperature gradient improvement, good heat insulation effect, Create a convenient effect

Inactive Publication Date: 2006-11-01
INST OF METAL RESEARCH - CHINESE ACAD OF SCI
View PDF1 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The common disadvantage of these heat insulation baffles is that the shape and size of the heat insulation baffle cannot be changed according to the shape and size of the formwork. A large amount of radiation is lost to the outside world between the hot rings, especially the heat radiated to the cooling zone seriously affects the temperature gradient between the upper and lower zones
Another disadvantage of the structure of corundum ring and molybdenum sheet is that it is inconvenient to use, requires complicated preparation process and subsequent processing to make, high cost, and difficult to make complex shapes
In addition: the corundum ring is easy to crack in high temperature use, thus affecting its heat insulation effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Heat-insulated baffle for oriented freezing cast
  • Heat-insulated baffle for oriented freezing cast
  • Heat-insulated baffle for oriented freezing cast

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0017] The following will be described in detail in conjunction with examples.

[0018] Such as figure 1 As shown, for a specific formwork (1), the heat insulation baffle (2) uses 70mm thick graphite hard felt, graphite hard felt, which can be obtained from relevant suppliers, such as SIGRATHERM graphite produced by Germany SGL Carbon Materials Group Hard felt, graphite hard felt produced by China Liaoyang Carbon Products Factory, etc. Graphite hard felt has a multi-layer structure, at least one surface has graphite paper, and the middle part is graphite fiber. The outer ring is connected with the mold holding furnace by cutting or cutting technology. The furnace body (3) is tightly combined, and the shape and size of the inner figure are consistent with the shape and size of the outer ring of the mold shell used, so that the gap (4) between them is controlled at 0.5mm, and at the same time, when the mold shell is pulled up and down, the movement of the mold shell will not be ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to view more

Abstract

A heat isolating plate for the directionally solidified casting is composed of two or more plates for splicing them together to become a single one, an external ring matched with the internal surface of temp holding furnace tightly, and an internal ring matched with the mould casing but retaining a gap (0.5-10 mm) between them for moving the mould casing easily. Said plate is just combined hard graphite felt.

Description

technical field [0001] The invention relates to directional solidification technology, in particular to a novel high-temperature heat insulation baffle applied to directional solidification equipment. Background technique [0002] In the traditional directional solidification process, the alloy ingot is melted and cast into the mold preheated in the holding furnace. The mold is placed on the water-cooled crystallizer, and the mold is gradually pulled out of the holding furnace at a certain speed to form a higher casting. Temperature gradient, which is the key to the formation of metal directional crystal structure. In order to achieve the maximum temperature gradient, the key is to minimize the heat radiation loss from the hot zone of the holding furnace to the outer cold zone of the holding furnace, so that the heat is mainly conducted through the water-cooled crystallizer and through the surface of the mold outside the holding furnace to the outside of the holding furnace....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B22D27/04
Inventor 张健燕冰川楼琅洪
Owner INST OF METAL RESEARCH - CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap