Production method of high solid content melamine resin

A melamine resin and melamine technology are applied in the formulation of high solid content melamine resin and the field of preparation thereof, which can solve the problems of increasing the cost of environmental protection treatment, difficult to accurately control the end point, fluctuating resin solid content, etc., and reduce investment costs. , the effect of avoiding the concentration stage and reducing the production cost

A melamine resin and melamine technology are applied in the formulation of high solid content melamine resin and the field of preparation thereof, which can solve the problems of increasing the cost of environmental protection treatment, difficult to accurately control the end point, fluctuating resin solid content, etc., and reduce investment costs. , the effect of avoiding the concentration stage and reducing the production cost

CN1903905AInactive Publication Date: 2007-01-31濮阳绿寰宇化工有限公司
0 Cites 13 Cited by

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Melamine 1500; paraformaldehyde 735; liquid formaldehyde (37%) 1200; sodium metabisulfite 100; dicyandiamide 150; o-cresol 48; methanol 150.

[0021] A final product of melamine resin with a solid content of 76%; a viscosity of 150 Pa.S; a density of 1.26; and a pH of 9.2 was obtained.

Embodiment 2

[0023] Melamine 1500; paraformaldehyde 735; liquid formaldehyde (concentration 37%) 1200; sodium metabisulfite 75; benzomelamine 225; methanol 150.

[0024] A melamine resin final product with a solid content of 76%; a viscosity of 140 Pa.S; a density of 1.28; and a pH of 9.0 was obtained.

Embodiment 3

[0026] Melamine 1500; paraformaldehyde 735; liquid formaldehyde (37%) 1200; sodium metabisulfite 100; polyvinyl alcohol 20; methanol 150.

[0027] A melamine resin final product with a solid content of 76%; a viscosity of 120 Pa.S; a density of 1.24; and a pH of 9.4 was obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to a formula of high solid content melamine resin and its preparation method. Said melamine resin is made up by using melamine, liquid formaldehyde (industrial product concentration is 37%) or paraformaldehyde and blending material through a synthesis process. The described material can be one of urea, monohydroxy-melamine, dihydroxy-melamine, alkyl-substituted melamine, polyvinyl alcohol, ethyl alcohol, ethylene glycol, methyl alcohol and others or their mixture. Said resin cam be used for producing melamine foamed plastics.

Description

technical field [0001] The invention relates to a formula and a preparation method of a melamine resin with high solid content, and the resin is especially suitable for the production of melamine foamed plastics. Background technique [0002] As we all know, melamine resin (melamine resin) has been used for more than half a century in the production of what is called "melamine molding compound" that meets food hygiene requirements. Melamine resins and amino resins modified with melamine have been widely used in the production of coatings, wood adhesives, impregnated paper adhesives and other products. In addition, in fine chemicals such as paper wet strength agent, fabric stiffening agent, fluorescent whitening agent, waterproofing agent, concrete water reducing agent, color paste, seed, fertilizer, pigment, dye capsule and serialized flame retardant The production field of the product has also been widely used. [0003] Since the 1980s, the research work on developing new...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
31 Jan 2007
Publication
CN1903905A
IPC
C08G12/38
Inventors
陈留拴; 王福田