Preparation method of cathode carbon block set for aluminum electrolytic cell

A cathode carbon block and aluminum electrolytic cell technology, which is applied in the direction of material forming presses, presses, manufacturing tools, etc., can solve the problems of high iron-carbon contact pressure drop, red steel rods, and uneven cathode current distribution, etc., to achieve Effects of reducing iron-carbon contact pressure drop, increasing iron-carbon contact area, and reducing primary defects

Active Publication Date: 2007-03-07
GUIZHOU BRANCH CHINA ALUMINUM IND
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

A common disadvantage of them is that the iron-carbon contact pressure drop is high
In addition, due to the thermal shock and the difference in thermal expansion between the carbon steel and the phosphorus pig iron casting method, cracks on both wings and corners of the cathode carbon block will cause hidden dangers for damage to the bottom of the electrolytic cell in the future.
The carbon paste tamping method has low strength after tamping. During the process of hoisting and placing carbon blocks, the steel rods will fall to varying degrees, resulting in uneven distribution of cathode current during roasting, which will easily make the steel rods red and the electrolytic cell Early damage, etc.
After the steel rod tamping paste is started and roasted and heated in the electrolytic cell, it will shrink volatilely, and the formed porosity is relatively large, which lays a hidden danger for the damage of the electrolytic cell

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of cathode carbon block set for aluminum electrolytic cell
  • Preparation method of cathode carbon block set for aluminum electrolytic cell

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0017] 1. Pretreatment of cathode steel rods: after sand washing or chemical method derusting of cathode steel rods, the prepared graphite powder paste (artificial graphite powder 50%-90%, binder 10%-50%, mix well) Apply evenly to the surface of the steel rod.

[0018] 2. Paste kneading: According to the conventional kneading process, the cathode paste is produced.

[0019] 3. Integrated molding: Firstly, an inner lining template 5 is added to the end of the mold 1 placed on the vibration platform 6 of the vibration forming machine, and a small groove is opened at the bottom of the inner lining plate to place and fix the 4 heads of the steel rod. When molding, at first a layer of paste 3 is spread on the bottom of the mold; (reserving a margin for bottom surface processing), the thickness is 20-50mm, and the weight 2 is lowered for static compaction. Lift the heavy hammer, place the cathode steel rod, and roughen the rest of the paste with steel claws. Add the remaining past...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparing method of cathode coke on the bottom of aluminium electrolytic groove bottom, which is characterized by the following: placing cathode steel bar in the slurry; vibrating; moulding the block inserted by cathode steel bar; sintering; manufacturing mechanically.

Description

technical field [0001] The invention discloses a production method of a cathode carbon block group for an aluminum electrolytic cell, relating to a method for manufacturing a cathode carbon block group used to form the furnace bottom of an aluminum electrolytic cell during the electrolytic aluminum production process. Background technique [0002] The cathode carbon block group is the main material constituting the furnace bottom of the aluminum electrolytic cell. The quality of its production directly affects the technical indicators such as the life of the electrolytic cell and the pressure drop of the furnace bottom. At present, the production process of the cathode carbon block group mainly includes the following two processes: [0003] A. Production of cathode carbon blocks: At present, the cathode carbon blocks used in aluminum electrolytic cells use electric calcined anthracite as the main raw material, adding different amounts of artificial graphite chips, and adding...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C25C3/08
CPCB30B11/022
Inventor 刘风琴苏自伟罗英涛
Owner GUIZHOU BRANCH CHINA ALUMINUM IND