Fine grained aluminium alloy and its preparing method

An aluminum alloy and fine-grain technology, which is applied in the field of fine-grained aluminum alloy and its preparation, can solve the problems of low element recovery rate, large variation, and high cost of intermediate alloys, and achieves the advantages of reducing cost, ensuring quality and improving recovery rate. Effect

Inactive Publication Date: 2007-03-28
DONGHUA UNIV
View PDF4 Cites 57 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the refinement effect of the master alloy is closely related to its microstructure and varies greatly
Their manufacturing process is not easy to master, and the refinement effect of each batch of alloys is different, which affects the quality of aluminum and aluminum alloy products
In addition, the cost of the master alloy is high, and the recovery rate of each element is low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fine grained aluminium alloy and its preparing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0051] In the 60KA electrolytic cell, add iron-removing silicon-titanium alumina powder (containing a small amount of boron oxide and rare earth oxide). Aluminum alloys containing low titanium, boron, rare earth and silicon are produced directly by electrolysis in cryolite system electrolyte. Adjust the chemical composition in the aluminum mixing furnace. The chemical composition of the electrolytic ZL101 aluminum-silicon alloy is as follows (mass fraction, %): Si7.24, Mg0.36, Fe0.11, Ti0.11, B0.0001, RE0.036. The average grain size of the α primary dendritic aluminum phase is 350 μm (Fig. 1). The average grain size of ZL101 alloy (titanium content is 0.10-0.15%) treated with Al-Ti master alloy under the same process conditions is 700 microns.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a refined crystal grain aluminum alloy and the manufacturing method. It is made up from Si 0.2-7.5wt%, Mn 0.05-1.5wt%, Mg 0,05-6.0wt%, Zn 0.03-8.5wt%, Cu 0.05-7.0wt%, Ni 0.1-2.5wt%, Ti 0.01-0.15wt%, RE 0.01-0.3wt%, B 0.0001-0.10wt%, and the rest is Al. The technology feature is that it adds silicon titanium alumina, borax and or rare earth oxide or rare earth carbonate, or titanium oxide, borax and / or rare earth oxide or rare earth carbonate into aluminum cell. Add the manganese oxide, compound of copper or Ni would be also added. Comparing to traditional technology, the refiner is not added, and the refining effect is enhanced and the perdurability is prolonged. It could be used to produce wire, band, tube, panel, aluminum foil, etc.

Description

technical field [0001] The present invention relates to a kind of aluminum alloy of fine grain and preparation method thereof, more precisely add silicon titanium aluminum oxide or titanium oxide and borax and / or rare earth oxide or rare earth carbonate (when needed Manganese oxide, copper compounds or nickel compounds can also be added), and these compounds are directly electrolyzed to obtain fine-grained aluminum alloys containing refined elements titanium, boron and / or rare earths, and then other chemical components are adjusted in the aluminum mixing furnace . The present invention does not use master alloy type refiners. Background technique [0002] Fine-grained aluminum alloy has good plasticity and punchability, and is an ideal material for the production of wire, strip, pipe, plate, aluminum foil, engine cooling fins, beverage cans, and auto parts. [0003] At present, there are three types of methods for refining aluminum or aluminum alloy grains: [0004] 1. Ch...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C21/00C22C1/00C22C1/03C22B1/02C25C1/02
Inventor 王汝燿杨冠群焦占忠
Owner DONGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com