Process for preparing core-shell structure TiO2/CaCO3 composite white pigment

A white pigment, shell structure technology, applied in inorganic pigment processing, chemical instruments and methods, fibrous fillers, etc., to reduce costs, improve whiteness and opacity, and avoid agglomeration effects

Active Publication Date: 2007-04-11
SHANGHAI DONGSHENG NEW MATERIALS
View PDF4 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Its role in reducing the amount of titanium dioxide and reducing costs is limited

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Process for preparing core-shell structure TiO2/CaCO3 composite white pigment
  • Process for preparing core-shell structure TiO2/CaCO3 composite white pigment
  • Process for preparing core-shell structure TiO2/CaCO3 composite white pigment

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Add raw gypsum and water to the reactor to prepare 0.817L of a suspension with a calcium sulfate content of 150g / L, add 10g of anatase titanium dioxide, and stir well; add 1.42g of lithium sulfate to control the calcium ion concentration of the system at about 2× 10 -5 mol / L; prepare 1.66L of potassium carbonate solution with a concentration of 75g / L; add the potassium carbonate solution to the calcium sulfate-titanium dioxide mixed suspension within 2 hours, so that calcium carbonate particles are slowly generated and deposited on the surface of titanium dioxide particles to form a shell , to obtain a composite material with a core-shell structure; the obtained suspension is filtered, washed, and dried at 110°C to prepare a composite white pigment dry powder containing 10% titanium dioxide. The obtained product was observed with a transmission electron microscope, and the particles showed a core-shell structure.

[0027] Paper filling experiment: beating according to ...

Embodiment 2

[0032] Add plaster of paris and water into the reactor to prepare 2.723L of a suspension with a calcium sulfate content of 10g / L, add 80g of rutile titanium dioxide, and stir well; add 0.043g of sodium bisulfate to control the calcium ion concentration of the system at about 5× 10 -4 mol / L; prepare 0.38L ammonium carbonate solution with a concentration of 50g / L; add the ammonium carbonate solution to the calcium sulfate-titanium dioxide mixed suspension within 8 hours, so that calcium carbonate particles are slowly generated and deposited on the surface of titanium dioxide particles to form a shell , to obtain a composite material with a core-shell structure; the obtained suspension is filtered, washed, and dried at 110° C. to prepare a composite white pigment dry powder containing 80% titanium dioxide. The resulting product was observed with a transmission electron microscope, as shown in Figure 1, the particles had a core-shell structure.

[0033] Adopt the method identical...

Embodiment 3

[0037] Add anhydrite and water into the reactor to prepare 1.7L of a suspension with a calcium sulfate content of 40g / L, add 50g of anatase titanium dioxide, and stir well; add 0.52g of sodium bisulfate and 0.68g of sodium sulfate, and the The concentration is controlled at about 5×10 -5 mol / L; the preparation concentration is 250g / L sodium bicarbonate solution 0.168L; add the sodium bicarbonate solution into the calcium sulfate-titanium dioxide mixed suspension within 6 hours, so that calcium carbonate particles are slowly generated and deposited on the surface of titanium dioxide particles to form shell layer to obtain a composite material with a core-shell structure; the resulting suspension is filtered, washed, and dried at 110° C. to prepare a composite white pigment dry powder containing 50% titanium dioxide. The obtained product was observed with a transmission electron microscope, and the particles showed a core-shell structure.

[0038] Adopt the method identical wit...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention discloses preparation process of white composite TiO2 / CaCO3 pigment in core-shell structure. The preparation process includes the following steps: adding titania into calcium sulfate suspension, adding calcium ion concentration regulator to control the calcium ion concentration in 2x10<-5>-5x10<-4> mol / L, and adding carbonate solution to produce the composite material in core-shell structure inside the suspension. The present invention has simple preparation process, stable product performance, and compact CaCO3 shell structure to avoid agglomeration of titania particle. The prepared white pigment has low cost and may be used in paper filler and paint to replace available titanium white powder for raised product quality.

Description

technical field [0001] The present invention relates to TiO 2 / CaCO 3 The preparation method of composite white pigment, specifically, relates to the TiO2 with core-shell structure of white pigment for papermaking 2 / CaCO 3 Preparation method of composite white pigment. Background technique [0002] Titanium dioxide (TiO 2 ), commonly known as titanium dioxide, is by far the most excellent white pigment. It has stable physical and chemical properties, excellent hiding power, tinting power, light and heat stability, and is widely used in coatings, plastics, papermaking, chemical fiber, ink, rubber and other fields. There are two main crystal forms of titanium dioxide, namely anatase and rutile, the latter having better hiding power and weather resistance. With the development of the world economy and the advancement of human science and technology, the application fields of titanium dioxide are becoming wider and wider, and the market demand for titanium dioxide is also...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09C1/36C09C1/02C09C3/06
Inventor 施晓旦许晓琳李丽
Owner SHANGHAI DONGSHENG NEW MATERIALS
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com