Manganese deoxidier and its preparation method and application

A deoxidizer and manganese-based technology, applied in the direction of chemical change purification/separation, etc., can solve the problems of low deoxidation capacity and high regeneration temperature, achieve large deoxidation capacity, improve mechanical strength, and prolong the effect of regeneration cycle

Inactive Publication Date: 2007-05-02
CHINA PETROLEUM & CHEM CORP +1
View PDF3 Cites 40 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] In order to overcome the defects of activation, regeneration, high use temperature and low deoxidation capacity of existing deoxidizers, the present invention pr

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～4

[0046] Weigh 420g triangular rhomboid MnCO 3 Fine powder, 60g pseudo-boehmite powder (bulk density 0.28g / ml, specific surface area 280m2 after roasting at 450°C 2 / g, weight loss 25%), 60g CaO fine powder, the three are fully mixed. Add an appropriate amount of distilled water and knead well. Then use extruder to prepare strips of Φ5; place overnight and dry in the air; dry at 120°C for 3 hours; cut into small sections with a length of 3 to 5 mm after cooling. The sample was evenly divided into 4 parts, which were respectively fired at 350, 400, 450, and 500° C. under an air atmosphere for 4 hours (Examples 1-4). Take a small amount of samples and use X-ray energy spectrometer to analyze the Mn of four deoxidizers 3 o 4 、Al 2 o 3 , CaO content. Take 50ml of deoxidizer respectively and put them into a Φ25 stainless steel reactor, and pass H at 280°C 2 Reduction 12h, H 2 Airspeed is 10h -1 . After cooling down, under the pressure of 0.4Mpa, respectively at the tempera...

Embodiment 5～8

[0049] According to the trigonometric rhombohedral MnCO 3 : Pseudoboehmite (bulk density 0.28g / ml, specific surface area 260m2 after calcination at 450°C 2 / g, weight loss 24%): CaO is respectively with weight ratio 7: 2: 0.5 (embodiment 5), 7: 3: 0.25 (embodiment 6), 7: 1: 2 (embodiment 7), 7: 3 : 0.5 (embodiment 8) prepares four parts of samples, fully mixes, each adds appropriate amount of 1.0% dilute nitric acid and kneads, then prepares the strip shape of Φ5 with extruding machine; Place overnight, dry in the air; 120 ℃ of oven dry 3 hours ; After cooling, cut into small sections with a length of 3 to 5 mm. It was then fired at 450°C for 4 hours in an air atmosphere. The prepared deoxidizer was activated and evaluated under the same operating conditions as in Example 1, and the evaluation results are shown in Table 2.

[0050] Example

Embodiment 9

[0052] 10 grams of MgO was used to replace 10 grams of CaO powder in Example 3, and the deoxidizer was prepared, activated and evaluated under the same conditions as in Example 3. The results are shown in Table 3.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

This invention discloses a deoxidizer of manganese system and its preparation and application. The deoxidizer of this invention is using MnO/Mn3O4 as active constituent. Add alkali metal oxide and aluminium oxide that are active accelerators. This invention provides two preparations, which adopt precurosor compound of Mn3O4 or active Mn3O4 that is produced by calcining precurosor compound of Mn3O4 to mix with alkali metal oxide or hydroxide oxide and aluminium, kneading, forming, open-air drying, at last drying or then producing deoxidizer of this invention by calcining after drying. The deoxidizer of this invention can eliminate 1- 2000ppm oxygen which is in the aethylenum or propylene, at the same time it possesses fairly high mechanical strength.

Description

technical field [0001] The present invention relates to a kind of manganese series deoxidizer and its preparation method and application, more specifically, the present invention relates to a kind of MnO / Mn 3 o 4 A high-capacity and high-activity deoxidizer as an active component, a preparation method and application thereof. Background technique [0002] Ethylene and propylene are important basic organic chemical raw materials, which generally contain trace oxygen. According to the national standard GB7715-87 for ethylene raw materials and GB7716-87 for propylene raw materials, the oxygen content in qualified polymer grade ethylene and propylene is ≤5ppm (5×10 -6 V / V, the same below). With the rapid development of polyethylene and polypropylene technology, various new high-efficiency polyethylene and polypropylene catalysts, such as: BCG, BCH, DQ, PZ, metallocene catalysts, etc. have been used in industrial production. In order to avoid poisoning and deactivation of suc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C07C7/148
Inventor 吕顺丰秦燕璜黄凤兴吴秀香
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap