Crystalline superfine particles, complex material, method of manufacturing crystalline superfine particles, inverted micelles, inverted micelles enveloping precursor superfine particles, inverted micelles enveloping crystalline superfine particles, and precursor superfine particles

Abstract

Crystalline superfine particles capable of emitting light depending upon a time-rate-of-change of a stress and controlled in grain size in the range from 5 nm to 100 nm are complexed with another material such as resin. The crystalline superfine particles are manufactured by using aggregates of molecules, i.e. inverted micelles, which orient hydrophilic groups of surfactant molecules inward and hydrophobic groups outward in a nonpolar solvent and which contain metal ions of a metal for forming the crystalline superfine particles dissolved in water inside the inverted micelles. Alternatively, they are manufactured by using inverted micelles enveloping precursor superfine particles, in which precursor superfine particles are enveloped in water inside the inverted micelles. The crystalline superfine particles are excellent in dispersibility in another material to be complexed, enhanced in emission efficiency and usable to make a transparent stress emission material. The complex material obtained is used to manufacture artificial light-emitting hair structures, artificial light-emitting skin, artificial light-emitting bodies, artificial light-emitting fabrics, and others.

Description

BACKGROUND OF THE INVENTION [0001] 1. Field of the Invention [0002] The present invention relates to crystalline superfine particles, complex material, method of manufacturing crystalline superfine particles, inverted micelles, inverted micelles enveloping precursor superfine particles, inverted micelles enveloping crystalline superfine particles and precursor superfine particles that are suitable for use in manufacture of a complex material used in, for example, the field of entertainment, the field of amusement or the field of optics. [0003] 2. Description of the Related Art [0004] For years, aluminate compound materials doped with rare earth elements have been remarked as fluorescent materials, and have been under vigorous researches. Among various aluminate compound materials, Eu-doped SrAl2O4 (written as SrAl2O4:Eu herein below) has attracted the greatest attention as from a report on the phenomenon of stress emission as introduced later. Thus, prehistory of researches and deve...

AI Technical Summary

Benefits of technology

[0023] That is, an object of the invention is to provide crystalline superfine particles as stress emission articles that are excellent in dispersibility when complexed with other materials, enhanced in emission efficiency, and suitable for preparing transparent stress emission materials.

[0139] Furthermore, when artificial light-emitting hair or artificial light-emitting fiber is manufactured from the complex material, the artificial light-emitting hair or the artificial light-emitting fiber can emit light easily only with a light hand or finger of a person. Further, emission of light stops immediately after removal of the touch. Thus, the user can induce and acknowledge emission of light by giving a light touch to the product, and can feel comfortable with it, or it effectively induce his / her interest.

Problems solved by technology

However, he describes or suggests nothing about development of their applications to artificial light-emitting skins, artificial light-emitting hair, artificial light-emitting bodies, artificial light-emitting cloth, and like others, for the purpose of entertainment.

However, there is no disclosure or suggestion on developments of applications to artificial light-emitting skins, artificial light-emitting hair, artificial light-emitting bodies, artificial light-emitting cloth, and like others, for the purpose of entertainment.

Therefore, it was difficult to obtain stress emission particles of a uniform grain size, and the grain size was as large as several μm.

Accordingly, it has been difficult to obtain complex materials in which stress emission particles are uniformly dispersed.

Moreover, it was difficult to apply stress emission particles to devices having micro-sized structures.

For example, in case of preparing stress emission artificial hair by packing stress emission particles in transparent tubes, a limit of downsizing the diameter of the tubes will make it difficult to obtain sufficiently thin stress emission artificial hair.

Furthermore, since stress emission particles having a grain size as large as several μm scatter and reflect light in the range of visible light (wavelengths from 400 to 750 nm), it was impossible to prepare transparent stress emission materials from those stress emission particles.

Therefore, the conventional stress emission particles are not suitable for use in portions such as a display panel required to be transparent, with which it is necessary to confirm information on one surface of the panel from the opposite surface through the panel.