Production baking-free natural-minerals adsorptive filter block

Abstract

A process for preparing the non-calcined natural minerals adsorbing-filtering block includes such steps as adding the calcined natural minerals adsorbing-filtering agent into stirrer, adding cement, quartz sand and water, stirring, filling the mixture into mould, pressing, conventional curing, and natural drying. It can be used to clean the animal or plant cultivating water.

Description

Technical field: [0001] The invention relates to a filter block, in particular to a production method of a burning-free natural mineral adsorption filter block. Background technique: [0002] In order to improve the production efficiency and economic benefits of aquaculture water, most of the farms adopt high-density intensive cultivation. The balance ability of the water ecosystem is limited. High-density intensive cultivation and a large amount of feeding can easily cause insufficient dissolved oxygen in the water body, resulting in a large amount of organic matter in the water. , the algae grow too fast, the water color changes greatly, the pH value is unstable, and the ammonia nitrogen content exceeds the standard. In order to maximize the production capacity of the limited aquaculture water body, it is necessary to maintain good water quality environmental conditions, which must solve the water quality pollution caused by the corruption of organic matter such as loose, ...

AI Technical Summary

Problems solved by technology

[0006] 1. The porous ceramic blank contains attapulgite rods. After being sintered at a constant temperature in the range of 1000-1500°C for 3-5 hours in the kiln, the crystal structure of the attapulgite rods has been severely damaged, which greatly reduces the attapulgite. Adsorption performance

[0007] 2. After the cement, gypsum, quartz sand and attapulgite in the ingredients are put into the kiln and sintered at a constant temperature within the range of 1000-1500 °C for 3-5 hours, they are in a molten state, and the voids formed by the bubbles produced by the foaming agent It will be greatly reduced, so it will cause poor sewage interception ability, low film-hanging efficiency, which is not conducive to the growth and reproduction of biological bacteria, and cannot effectively reduce the ammonia nitrogen content of aquaculture water.