C100 high-performance concrete and formulation method thereof

A technology of high-performance concrete and cementitious materials, applied in the direction of climate sustainability, sustainable waste treatment, solid waste management, etc., can solve the problems of complex production process and high manufacturing cost, achieve good work performance, low The effect of reducing cost

Active Publication Date: 2009-07-08
北京新奥混凝土集团有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0014] The purpose of the present invention is to provide a kind of C100 high-performance concrete and preparation method thereof, solve the problems that existing C100 high-performance concrete preparation needs special raw materials such as high-grade cement, complex production process, and high manufacturing cost; The technical problem of improving the workability and durability of concrete while increasing the strength

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0041] Embodiment: this C100 high-performance concrete is formed by mixing and gelling cementitious material, sand, stone, water and admixture, and comprises cement and admixture in the cementitious material, is characterized in that: the adding of cementitious material The amount is 500-600kg per cubic meter of concrete, of which,

[0042] Cement: 42.5 cement;

[0043] Admixture: silicon powder active SiO with an amount of 20% to 40% of the total weight of the cementitious material 2 , its specific surface area is 1050m 2 / kg;

[0044] Admixture: polycarboxylate high-efficiency water reducer with an amount of 2% to 5% of the total weight of the gelling material;

[0045] The solid content of the polycarboxylic acid high-efficiency water reducer is 18% to 30%, and the water reducing rate is 30% to 45%.

[0046] The above-mentioned 42.5 cement is ordinary Portland 42.5 cement or Portland 42.5 cement.

[0047] Besides silicon powder, the admixture also contains fly ash and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
slumpaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

A C100 high-performance concrete, which is formed by mixing and gelling cementitious materials, sand, stone, water and admixtures. The cementitious materials include cement and admixtures. The amount of cementitious materials added per cubic meter of concrete 500-600kg, of which the cement is 42.5; the admixture has three components of silica fume, fly ash and slag powder, and contains active SiO2 in an amount of 20%-40% of the total weight of the cementitious material, and its specific surface area 1000-1200m2 / kg; the admixture is polycarboxylate high-efficiency water reducer with a dosage of 2% to 5% of the total weight of the cementitious material; the activator is soot and coal with a dosage of 1 to 5% of the total weight of the cementitious material A mixture of gangue fine powder. No special raw materials such as high-grade cement are needed, the production process is simple, and the manufacturing cost is low. While greatly improving the strength of concrete, it also improves the workability and durability of concrete.

Description

technical field [0001] The invention relates to a building concrete material and a preparation method thereof. Background technique [0002] With the development of urban construction and the progress of construction technology, higher requirements are put forward for concrete quality indicators and economic indicators, and the development of concrete is promoted towards high performance such as high strength, light weight, fluidity, and durability. [0003] Especially in the past ten years, due to the development of high-efficiency admixtures and concrete admixture technology, favorable technical conditions have been provided for the preparation of high-strength and high-performance concrete under common process conditions. In the design of some large-scale structures, railway engineering and municipal engineering, more concrete with grades of C50 and C60 appeared. C100 high-performance concrete has also been a hot spot in the research of concrete materials at home and abro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/04C04B14/06C04B18/08C04B18/14C04B24/24
CPCC04B40/0039C04B28/02Y02W30/91C04B14/04C04B18/08C04B18/141C04B14/02C04B14/022C04B14/06C04B18/146C04B20/0076C04B40/0028C04B2103/302C04B24/2641
Inventor 路来军马雪英王安领
Owner 北京新奥混凝土集团有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products