High molecule fascia and method for preparing the same

A polymer and bandage technology, applied in bandages, medical science, absorbent pads, etc., can solve the problems of non-decreasing adhesiveness of bandages and single color, and achieve the effect of product color diversification

Active Publication Date: 2008-01-02
BEIJING JINWEI KANGDA MEDICAL INSTR LTD
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The bandage provided by the invention and its manufacturing method can further overcome the technical problem of single color of existing products, and the adhesiveness of the bandage after curing will not decrease.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] First heat the polyether (polyether GE210 produced by Shanghai Gaoqiao Chemical Factory) at a pressure of about -0.1Mpa to 80°C, keep the temperature constant for 30 minutes, and then heat again. When the temperature rises to 100°C, keep the temperature constant for 30 minutes and continue heating, and when the temperature rises to 120°C, keep the temperature constant for 60 minutes for later use.

[0027] Under the conditions of stirring and nitrogen blanketing, first add liquid diphenylmethane diisocyanate (isocyanate MSBASF product) at a temperature of 50 ° C, and then add polyether in a dropwise manner, with a dropping rate of 10 c / min and a stirring speed of 100 rpm Then, heat the reaction material to 70°C and use cold / hot water double temperature control method to stabilize the temperature at 80°C for 1 hour, then cool down to 60°C, and finally add various additives, including stabilizers, catalysts, Defoamer, filler (nano-calcium carbonate Shanghai Gerunya Nano M...

Embodiment 2

[0035] Under the conditions of stirring and nitrogen blanketing, first add liquid carbodiimide modified MDI at a temperature of 50 °C, and then add polyether in a dropwise manner, with a dropping speed of 10 c / min and a stirring speed of 100 rpm, and then Heating the reaction material to 70°C, adopting double temperature control method of cold / hot water, keeping the temperature at 80°C for 1 hour, then cooling down to 60°C, and finally adding various additives. At this point the stirring speed was increased to 200 rpm for 1 hour. Under the protection of nitrogen, the discharged material is put into a container for use. The polyurethane prepolymer has a viscosity of 1200 centipoise at 50° C. and an NCO% content of 15.

[0036] In the bandage prepared by the above method, the polyurethane prepolymer accounts for 40% by weight of the bandage (the same below), the catalyst content is 2%, and the particle diameter of the filler is less than 100nm, and its content is 2%.

[0037] ...

Embodiment 3

[0040] Under the conditions of stirring and nitrogen blanketing, first add the liquid MDI / carbodiimide modified MDI mixture at a temperature of 50°C, and then add the mixed polyether in a dropwise manner, the dropping speed is 10c / min, and the stirring speed is 100 rpm / min, then heat the reaction material to 70°C, use cold / hot water double temperature control method, stabilize the temperature at 80°C for 1 hour, then cool down to 60°C, and finally add various additives, including stabilizers, catalysts , defoamer, filler and liquid paste. At this point the stirring speed was increased to 200 rpm for 1 hour. Under the protection of nitrogen, the discharged material is put into a container for use. The polyurethane prepolymer has a viscosity of 1100 centipoise at 50° C. and an NCO% content of 15.

[0041] In the bandage prepared by the above method, the polyurethane prepolymer accounts for 35% by weight of the bandage (the same below), the catalyst content is 1.05%, and the p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a high polymer bandage and the preparation method, which solves problem of heterogeneous distribution of pre-polymer during bandage storage, and the adhesive effect of bandage is not reduced. The bandage is equipped with base raw material, the base raw material comprises polyurethane prepolymer, catalyst and packing material, the weight proportion of polyurethane prepolymer is 20-50% of that of bandage, the catalyst is amine compound, the proportion of it is 0.1-5%, and the granule diameter is smaller than 100nm and its proportion is 0.1-5%. The bandage can be widely used for fixation for surgery.

Description

Technical field: [0001] The invention relates to a surgical fixation material and a preparation method thereof, in particular to a polymer bandage and a preparation method thereof. Background technique: [0002] Plaster bandage is the most common external fixation material in orthopedic treatment. Although the method of applying plaster is an essential treatment procedure, it brings obvious discomfort to orthopedic patients. Due to fracture treatment, plaster bandages need to be applied for 3-10 weeks, resulting in long-term contact between the patient's skin and plaster. This can easily cause itching, discomfort and inflammation, and the plaster is bulky, poor in strength, inelastic after curing, airtight, and will soften or break after soaking in water. In addition, the X-ray transparency is poor. After the plaster is applied, X-ray film examination cannot be carried out effectively. This is not conducive to checking the progress of fracture treatment, so it is impossible...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61L15/20
Inventor 姚克俭康文斌李东春卢英芬
Owner BEIJING JINWEI KANGDA MEDICAL INSTR LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com