PC/ABS alloy waste recovering formula

A technology for waste recycling and formula, applied in the field of polymer material recycling formula, can solve the problems of waste, environmental pollution, not economical and practical, and achieve the effects of reducing production costs, avoiding environmental pollution, and improving social and economic benefits.

Inactive Publication Date: 2008-01-30
MITAC PRECISION TECH CO LTD SHUNDE DISTRICT FOSHAN CITY
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since PC/ABS alloys are widely used in electronic and electrical products, the amount of waste materials produced after such products are scrapped is very large. In order to reduce environmental pressure and energy consumption, and improve resource utilization efficiency, the traditional method of incinerating and burying waste materials The method is not economical and pract

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0042] Example 1

[0043] Weigh the following materials in proportion:

[0044] PC / ABS waste 48.8

[0045] High impact PC / ABS nozzle material 39

[0046] MBS 2

[0047] Decabromodiphenylethane 3

[0048] Antimony trioxide 1

[0049] Acrylic impact modifier 6

[0050] Antioxidant 1010 0.2

[0051] Then the blended material is mixed and granulated in an extruder, and the obtained mixed granulation is injected into a finished product. Finally, the mechanical properties of the finished product are tested according to the national standard GB13525 / T-92 and according to the American Electrotechnical Association UL94 standard Test its flame-retardant properties, and measure the melt mass flow rate (MFR) of the product in accordance with the national standard GB / T3682-2000. The results are compared with the performance of the PC / ABS waste and PC / ABS raw materials before the improvement, as shown in Table 1.

[0052] Table 1: Performance comparison between the product obtained in Example 1...

Example Embodiment

[0054] Example 2

[0055] Weigh the following materials in proportion:

[0056] PC / ABS waste 43.7

[0057] High impact PC / ABS nozzle material 43.7

[0058] MBS 2

[0059] Decabromodiphenylethane 4

[0060] Antimony trioxide 1.3

[0061] Acrylic impact modifier 4

[0062] Antioxidant 1010 0.3

[0063] Then the blended material is mixed and granulated in an extruder, and the obtained mixed granulation is injected into a finished product. Finally, the mechanical properties of the finished product are tested according to the national standard GB13525 / T-92 and according to the American Electrotechnical Association UL94 standard Test its flame retardant properties, and measure the melt mass flow rate (MFR) of the product in accordance with the national standard GB / T3682-2000. The results are compared with the performance of the PC / ABS waste and PC / ABS raw materials before improvement, as shown in Table 2.

[0064] Table 2: Performance comparison between the product obtained in Example 2...

Example Embodiment

[0066] Example 3

[0067] Weigh the following materials in proportion:

[0068] PC / ABS scrap 40

[0069] High impact PC / ABS nozzle material 52

[0070] MBS 1

[0071] Decabromodiphenylethane 3

[0072] Antimony trioxide 1

[0073] Acrylic impact modifier 2.6

[0074] Antioxidant 1010 0.4

[0075]Then the blended material is mixed and granulated in an extruder, and the obtained mixed granulation is injected into a finished product. Finally, the mechanical properties of the finished product are tested according to the national standard GB13525 / T-92 and according to the American Electrotechnical Association UL94 standard. Test its flame retardant performance, and measure the product's melt mass flow rate (MFR) according to the national standard GB / T3682-2000. The results are compared with the performance of the PC / ABS waste and PC / ABS raw materials before the improvement, as shown in Table 3.

[0076] Table 3: Performance comparison between the product obtained in Example 3 and PC / A...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The components containing in a recycle formula of PC/ABS alloy waste can be expressed in terms of mass fraction as 40 to 50 for PC/ABS waste, high-impact PC/ABS, 35 to 55 for regrinds, 1 to 3 for plasticizers, 3 to 7 for bromide fire retardant, 1 to 3 for stibium fire retardant, 2 to 7 for acrylic impact modifiers, and 0.2 to 0.5 for oxidation inhibitor. By mixing high-impact PC/ABS regrinds with general PC/ABS waste and adding various assistant, the formula of the invention can ensure that different properties of PC/ABS alloy waste meets the PC/ABS raw material standard, thereby, with quite good social and economic benefits, the formula can not only reduce production cost but also avoid the environmental pollution caused by the waste.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to a formula for recovering polymer materials. Background technique [0002] PC / ABS alloy is a kind of engineering plastic with good comprehensive performance developed in the mid-1960s. It not only has the heat resistance, mechanical strength and dimensional stability of PC, but also has the advantages of easy processability and low price of ABS resin. ; It has good comprehensive performance and reasonable cost performance, and can be widely used in the fields of automobile industry and household appliances. Since PC / ABS alloys are widely used in electronic and electrical products, the amount of waste materials produced after such products are scrapped is very large. In order to reduce environmental pressure and energy consumption and improve resource utilization efficiency, the traditional method of incinerating and burying waste materials The method is not economical a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L69/00C08L55/02C08K5/02C08L33/10C08K3/22
Inventor 汪克风岳瑟杨得志刘济林
Owner MITAC PRECISION TECH CO LTD SHUNDE DISTRICT FOSHAN CITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap