Mass acrylonitrile-butadiene-phenylethene and polyterephthalic acid butanediol fat compound and preparation method thereof

A technology of polybutylene terephthalate and acrylonitrile is applied in the field of chemical materials to achieve the effects of expanding the scope of application, dimensional stability and improving strength

Active Publication Date: 2010-09-08
SHANGHAI KINGFA SCI & TECH +1
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The mechanical properties of unreinforced PBT are only at the general level, but the various strengths and heat-resistant temperatures are greatly improved after being reinforced with glass fiber.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-3

[0027] Polybutylene terephthalate is one of Polyplastics’ PBT 3216, Taiwan Nanya’s PBT140EM, Yizheng Chemical Fiber’s PBT L2100 or a mixture thereof; the mass-process acrylonitrile-butadiene-styrene resin uses DOW The company's ABS3453; the compatibilizer is ABS-maleic anhydride graft copolymer, wherein the maleic anhydride graft rate is 0.8%-2.0%; The copolymer of N-phenylmaleimide and AS; the glass fiber is preferably prepared by Chongqing Composite Materials Co., Ltd., and the specification is glass fiber of ER5301-2000.

[0028] raw material name

Example 1

Example 2

Example 3

ABS3453

50

60

30

PBT 140EM

20

30

PBT L2100

20

ABS-maleic anhydride graft copolymer

7

7

5

Heat resistance modifier AS-MS-NA

3

3

5

Glass fiber ER5301-2000

20

10

30

[0029] Comparative formula

[0030] raw material name

Bulk method ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
Login to View More

Abstract

The present invention relates to a mass polymerization compound of an acrylonitrile- butadiene-cinnamene and poly-terephthalic acid butanediol lipid, which is characterized by consisting of the following weight percentage compositions of materials: 30-70 percent of mass polymerization acrylonitrile- butadiene-cinnamene (ABS) resin, 5-30 percent of poly-terephthalic acid butanediol lipid (PBT) resin, 2-8 percent of compatibilizer, 0.5-5 percent of heat resisting modifier and 10-35 percent of glass fibre, and the manufacturing method thereof is characterized in that under the high speed cut, milling and delivery of a screw, the material can be melted and compounded sufficiently, and the final product can be achieved after fusing, extruding a stray, cooling, pelleting and drying. The advantage of the present invention is to obtain the performance, such as high intension, fatigue resistance, shock resistance, of the mass polymerization acrylonitrile- butadiene-cinnamene (ABS), extending the application range of the mass polymerization acrylonitrile- butadiene-cinnamene (ABS).

Description

technical field [0001] The invention relates to a bulk-process acrylonitrile-butadiene-styrene and polybutylene terephthalate compound and a preparation method thereof, which has high heat resistance, high rigidity, fatigue resistance, stable size and warpage prevention, etc. function, can be applied to home appliances, IT, auto parts, and belongs to the technical field of chemical materials. Background technique [0002] Acrylonitrile-butadiene-styrene (ABS) resin combines the characteristics of general-purpose synthetic resins and engineering plastics, has high impact strength, heat resistance and dimensional stability, excellent comprehensive performance, and is easy to process. With various advantages, it is widely used in industrial spare parts, casings and transmission parts of electronic and electrical products, office equipment, and other fields. [0003] There are many production methods of ABS resin. At present, the most widely used industrial devices in the world...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L55/02C08K7/14C08L67/03
Inventor 杨定吉甫吉继亮梁荣朗袁绍彦吴晓辉夏建盟
Owner SHANGHAI KINGFA SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com