Shockproof conductive polyphenyl ether polyamide compound and method for making same

A technology for polyphenylene ether polyamide and compound, which is applied in the field of conductive polyphenylene ether polyamide compound and its preparation, can solve the problems of mechanical properties and processing properties being affected, and achieves excellent mechanical properties, good compatibility, The effect of improving mechanical properties

Active Publication Date: 2008-03-05
KINGFA SCI & TECH CO LTD +1
View PDF0 Cites 36 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to overcome the problem that the mechanical properties and processability of the existing conductive plastics are affected due to the addition of a large amount of carbon black, and to provide a method that can retain the excellent mechanical properties of polyphenylene ether and polyamide resin and whose surface resistance can reach 10 2 -10 10 Omega's impact-resistant conductive polyphenylene ether-polyamide composite

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Shockproof conductive polyphenyl ether polyamide compound and method for making same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] The preparation steps of the impact-resistant conductive polyphenylene ether polyamide compound of the present invention are:

[0021] Adopt high-speed pre-mixing and dispersing one-time extrusion process. First, the polyphenylene ether, polyamide resin, high impact polystyrene, phosphate ester, impact modifier, antioxidant, coupling agent and other additives are dispersed and mixed by a high-speed mixer, and then directly enter the twin-screw extruder Processing, carbon black or carbon fiber (or carbon nanotubes) enters the twin-screw extruder through side feeding for processing, and is extruded, cooled, dried, pelletized and packaged. The temperature of each partition of the screw barrel should be kept at 240-270°C. The aspect ratio of the twin-screw extruder is 38, and the screw speed is 400 rpm.

[0022] According to the above preparation method, the embodiment uses polyphenylene ether as polyphenylene ether with a characteristic viscosity of 0.40dl / g, the polyami...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to one kind of high molecular composite material, and is especially one kind of shock resisting conductive polyphenyl ether-polyamide composition and its preparation process. The polyphenyl ether composition consists of polyphenyl ether resin 30-50 wt%, polyamide 20-50 wt%, carbon black 0.3-25 wt%, shock modifier 3-20 wt% and phosphate 1-10 wt%. It is prepared through high speed pre-mixing and dispersing and once extruding. The polyphenyl ether-polyamide composition has high chemical resistance, high mechanical performance, easy forming and other advantages, and is suitable for use as package of electronic devices and in electrostatic coating parts.

Description

technical field [0001] The invention relates to a polymer composite material, in particular to an impact-resistant conductive polyphenylene ether polyamide compound and a preparation method thereof. Background technique [0002] Electronic devices need packaging containers to carry and protect them during production, transportation and use. In order to prevent damage to electronic devices caused by static electricity generated by friction between electronic devices and containers, these containers are all made of conductive plastic. become. [0003] The main components of existing conductive plastics are compounded by plastics, conductive carbon black, carbon fiber or carbon nanotubes and various additives. Carbon fiber and carbon nanotubes have the characteristics of small dosage and little impact on the mechanical properties of the material, but the cost is much higher than carbon black, and the market is currently mainly based on carbon black. [0004] The main plastic ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L71/12C08L77/00C08K5/521B29B9/12B29C47/40C08L53/02C08L25/08C08K5/13C08K3/04C08K5/36C08K5/25B29C48/40
CPCB29C48/40
Inventor 薄文海叶南飚蔡彤旻徐依斌
Owner KINGFA SCI & TECH CO LTD
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com