Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Weather-resistant hot rolled narrow steel strip and method for manufacturing same

A manufacturing method and technology for narrow steel strips, applied in metal rolling, manufacturing tools, metal rolling, etc., can solve the problems of high cost, complex production process, difficulty in marketization, etc., and achieve high production efficiency and reduce manufacturing costs. , Good effect of atmospheric corrosion resistance

Inactive Publication Date: 2008-03-05
LAIWU IRON & STEEL GRP
View PDF2 Cites 41 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the weather-resistant steel provided in the above patent documents improves the performance of the steel, the cost is too high, and the production process is complicated, so it is difficult to market

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0024] The present invention will be further described below in conjunction with the examples, but not limited thereto. Embodiment 1. The specification is a steel strip of 3.0mm×285mm, and the specification of the billet is 120mm×285mm.

[0025] 1. The chemical composition of steel is as follows by weight percentage:

[0026] C: 0.10%, Si: 0.33%, Mn: 0.38%, P: 0.100%, S: 0.021%, Cu: 0.30%, Cr: 0.53%, Ni: 0.12%, and the rest are Fe and unavoidable impurities.

[0027] 2. Manufacturing method of weather-resistant hot-rolled narrow steel strip

[0028] The process route is as follows:

[0029] Hot metal pretreatment - 40t top-blown converter smelting - LF ladle refining belt billet continuous casting - 500mm full hot continuous rolling mill rolling.

[0030]The pre-desulfurization of molten iron is to spray and passivate magnesium particles in the molten iron tank, so that the sulfur in the molten iron is controlled below 0.025%, the temperature is not lower than 1250°C, and t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to one kind of weather resistant hot roller narrow steel strip for welded structure and its production process. The steel strip has the chemical composition comprising C 0.07-0.12 wt%, Si 0.25-0.50 wt%, Mn 0.30-0.50 wt%, P 0.07-0.15 wt%, S less than 0.035 wt%, Cu 0.25-0.40 wt%, Cr 0.30-1.2 wt%, Ni 0.10-0.50 wt%, and Fe and inevitable impurity for the rest. It is produced through smelting in a top blown converter, LF refining, continuously casting steel strip billet and hot rolling in a continuous rolling mill train. It has high purity, excellent corrosion resistance, excellent welding performance and homogeneous mechanical performance. It may be applied in making square welded tube or other accessories for container.

Description

technical field [0001] The invention relates to weather-resistant steel and a manufacturing method thereof, belonging to the technical field of low-alloy steel, in particular to a weather-resistant hot-rolled narrow steel strip for container welding components and a manufacturing method thereof. Background technique [0002] Weathering steel is a general term for a class of steel resistant to atmospheric corrosion. The existing technology generally uses a large amount of alloying elements such as Cu, P, Cr, Ni, Al, etc. to the steel, and some also add As, Ce, Co, Ti, V and other elements to improve the weather resistance of steel and obtain proper strength. Chinese patent document CN1752260, application number 200510012897.0 discloses a "hot-rolled dual-phase weathering steel plate and its manufacturing method". C, 0.05-0.15% P, 0.1-0.4% Cu, Cr, Ni, Ti, V, Nb and other elements, the tensile strength is greater than 680MPa, the yield strength is greater than 360MPa, the elon...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C38/42C22C33/04C21C7/00C21D8/02B21B37/00B21C47/02B22D11/16
Inventor 周平汤化胜亓伟伟郭伟达费燕于全成王奉县王腾飞杨旭闫志华
Owner LAIWU IRON & STEEL GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com