Slurry blending printing method for fabric by using pearl nano particle

A nanoparticle and fabric technology, applied in the field of fabric printing, can solve the problems of poor fabric softness, hand feeling and comfort, high cost, complicated production process, etc., and achieve the effects of low cost, material saving, and simple process

Inactive Publication Date: 2008-07-02
程衍铭
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantage is that the production process is complicated, the cost is high, and the softness, feel and comfort of the fabric are poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Embodiment 1: the printing paste formula (1) of fabric same paste blending printing

[0025] Pearl nanoparticles (average particle size 100nm) 15g / l

[0026] Paint 20g / l

[0027] Adhesive acrylate resin 100g / l

[0028] Penetrant JFC 6g / l

[0029] Thickener M 22g / l

[0030] Dispersant NNO 12g / l

[0031] Urea 15g / l

[0032] Pinpinga 0 25g / l

Embodiment 2

[0033] Embodiment 2: the printing paste formula (2) of fabric homogeneous blending printing

[0034] Pearl nanoparticles (average particle size 100nm) 12g / l

[0035] Paint 22g / l

[0036] Adhesive acrylate resin 80g / l

[0037] Penetrant JFC 5g / l

[0038] Thickener M 20g / l

[0039] Dispersant NNO 10g / l

[0040] Urea 15g / l

[0041] Pingping plus 0 20g / l

Embodiment 3

[0042] Embodiment 3: the same paste blending printing process of pure cotton fabric:

[0043] Refining fabric→printing→pre-drying: 80°C, 4min→baking: 150°C, 1.5min.

[0044] The equipment used is a conventional rotary screen printing machine, and the operation requirements are the same as the conventional paint printing process.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for fabric co-mixed combination printing by using pearl nanoparticles in industrial textile production. A printing paste selected by the method contains pearl nanoparticels (mean diameter 100 nm) 10 to 20 g / l, coating 0 to 40 g / l, acrylate resin binding agent 80 to 120 g / l, penetrant JFC 5-7 g / l, thickening agent M 20 to 25 g / l, dispersant NNO 10 to 15 g / l, urea 15 to 18 g / l and peregal O 20 to 30 g / l. The co-mixed combination printing process comprises the steps of refining cloth, printing, pre-baking at 75 to 85 DEG C for 3 to 5 min and baking at 140 to 160 DEG C for 1 to 1.5 min, wherein the warp yarn and the weft yarn of the finish fabric have a fineness less than 27.8 tex, and the warp and the weft densities are larger than 425*228 piece / 10cm. The invention has the advantages of simple process, suitability for various fabric textile, co-mixture of pearl particles and printing paste, no additional finishing procedures, controllable size and distribution of pearl particle coating layer, less material consumption and low cost.

Description

technical field [0001] The invention relates to the technical field of fabric printing in textile industry production, in particular to a method for fabric blending and printing with pearl nanoparticles. Background technique [0002] Pearl powder is flexible, smooth and shiny, and has certain antibacterial, health care and skin care effects. The fiber containing pearl powder or the fabric coated with pearl powder has a pearly luster and a smooth and comfortable feel after being made into a textile fabric. [0003] At present, the production methods of fibers containing pearl powder or fabrics coated with pearl powder mainly contain the following. [0004] (1) Cotton-type pearl fiber is produced by wet blending spinning method. In this method, pearl particles are mixed into the spinning solution during the viscose production process, and the fiber is purely spun or blended with other fibers, and is processed into a textile fabric containing pearl particles through textile d...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06P1/673D06P1/58
Inventor 程衍铭陈平唐大钧
Owner 程衍铭
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com