Method for preparing high-bonding strength catbon steel based Al2O3 ceramic coating with colloidal sol-gel rubber

A combination of strength and ceramic coating technology, applied in coating, metal material coating process, superimposed layer plating, etc., can solve the problems of high cost, expensive laser processing equipment, and high requirements for ceramic oxide types, etc., to achieve The effect of good compactness, uniform composition and simple process

Inactive Publication Date: 2008-09-24
ZHEJIANG UNIV
View PDF0 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It was reported that by combining laser-assisted processing with sol-gel technology, Cr 2 o 3 and SiO 2 The powder is mixed with silica sol and coated on the metal so that it forms SiC and M 7 C 3 In order to i

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing high-bonding strength catbon steel based Al2O3 ceramic coating with colloidal sol-gel rubber
  • Method for preparing high-bonding strength catbon steel based Al2O3 ceramic coating with colloidal sol-gel rubber

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0018] Example 1:

[0019] Preparation of Al2O3 ceramic coating with good film-base bond strength on the surface of No. 20 steel. Process:

[0020] Electroless Ni-P alloy intermediate transition layer process:

[0021] Test process: The sample is ground, polished, cleaned and other pre-plating pretreatment → electroless nickel plating → hot water washing → water washing → drying under vacuum at 180 ° C for 1 hour.

[0022] Bath composition: nickel sulfate: 25g / L; sodium hypophosphite: 23g / L; sodium citrate: 8g / L and sodium acetate: 15g / L.

[0023] Process conditions: temperature: 85℃; pH value of plating solution: 4.0; plating time: 1-2h;

[0024] Coating Al on the Surface of Electroless Ni-P Coating by Sol-Gel Method 2 O 3 Ceramic coating process:

[0025] Select aluminum isopropoxide as a precursor, use secondary deionized water as a solvent, and use nitric acid as a peptizer in a molar ratio of 1:80:0.1, first mix the finely ground aluminum isopropoxide and deionized w...

Example Embodiment

[0029] Example 2:

[0030] Preparation of Al2O3 ceramic coating with good film-base bond strength on the surface of 45# steel:

[0031] Electroless Ni-P alloy intermediate transition layer process:

[0032] Test process: clean the surface of the sample for pretreatment → electroless nickel plating → cleaning → drying under vacuum at 190 °C for 1 hour.

[0033] Bath composition: nickel sulfate: 26g / L; sodium hypophosphite: 24g / L; sodium citrate: 10g / L and sodium acetate: 16g / L.

[0034] Process conditions: temperature: 87°C; pH value of plating solution: 5.0; plating time: 1.5h.

[0035] Coating Al on the Surface of Electroless Ni-P Coating by Sol-Gel Method 2 O 3 Ceramic coating process:

[0036] Select aluminum isopropoxide as a precursor, use secondary deionized water as a solvent, and use nitric acid as a peptizer in a molar ratio of 1: 100: 0.2, first mix the finely ground aluminum isopropoxide and deionized water, After vigorously stirring at a water bath temperatur...

Example Embodiment

[0040] Example 3:

[0041] Preparation of Al with good film-base bond strength on the surface of 60# steel 2 O 3 Ceramic coating:

[0042] Electroless Ni-P alloy intermediate transition layer process:

[0043] Test process: clean and pretreat the surface of the sample → electroless nickel plating → cleaning → drying under vacuum at 200°C for 1 hour.

[0044] Bath composition: nickel sulfate: 28g / L; sodium hypophosphite: 25g / L; sodium citrate: 12g / L and sodium acetate: 18g / L.

[0045] Process conditions: temperature: 90°C; pH value of plating solution: 6.0; plating time: 1.5h.

[0046] Coating Al on the Surface of Electroless Ni-P Coating by Sol-Gel Method 2 O 3 Ceramic coating process:

[0047] Select aluminum isopropoxide as a precursor, use secondary deionized water as a solvent, and nitric acid as a peptizer in a molar ratio of 1: 120: 0.3, first mix the finely ground aluminum isopropoxide and deionized water, After vigorously stirring at a water bath temperature of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Surface microhardnessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for preparing high bonding intensity carbon steel-based Al2O3 ceramic coat by sol-gel. The method adopts the carbon steel as a compound coating basic body, adopts nickel vitriol as main salt, adopts NaH2PO2 as a reducer to chemically plate a Ni-P alloy in an acid medium, takes aluminium isopropoxide as a precursor, takes secondary de-ionized water as a solvent and takes nitric acid as a glue solvent to prepare boehmite sol acordign to a mol ratio of 1:80 to 120: 0.1 to 03; adopts a dip-coating method to coat and then bake the gel. The invention takes a chemically plated Ni-P alloy as a middle transition layer and adopts the sol-gel method to prepare the Al2O3 ceramic coat on the surface of the carbon steel, thus solving the technical difficulty of the lower bonding force of the carbon steel-based ceramic coat. The compound processing method provided by the invention has a simple and convenient technique and needs no expensive and complex devices; besides, the prepared compound coat has excellent compactness and uniform components. The technique can be used for carbon steel anti-high temperature oxidation coat; the technique of the method is easy to realize industrialization and is not restrained by the shape of a workpiece.

Description

technical field [0001] The invention relates to the field of metal surface modification, in particular to a sol-gel technique for preparing carbon steel-based Al with high bonding strength 2 o 3 Ceramic coating method. Background technique [0002] Surface modification technology can improve the surface properties of metal materials, prevent or delay the failure of workpieces, and prolong the service life of workpieces and equipment, which has huge economic benefits. Ceramic materials have high hardness, good wear resistance, corrosion resistance and high temperature oxidation resistance. The preparation of ceramic coatings on metal surfaces can combine the above advantages of ceramic materials with the advantages of high plasticity and toughness of metal materials to obtain workpieces with good comprehensive properties. At present, the steel-based ceramic coating preparation techniques include powder metallurgy, plasma spraying, laser cladding, vapor deposition, enamel co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23C28/00C23C18/36C23C18/18C23C26/00C04B35/10
Inventor 郦剑罗来马
Owner ZHEJIANG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products