Powder metallurgy passenger car chain pulley and method for producing the same

A powder metallurgy and sprocket technology, applied in belts/chains/gears, mechanical equipment, portable lifting devices, etc., can solve the problems of affecting the service life of car sprockets, affecting service life, and high production costs, achieving easy installation, overall Good sex, light weight effect

Inactive Publication Date: 2008-10-01
吕元之
View PDF0 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantages of the sprocket for cars produced by machining technology are that it has a large specificity, and the assembly with the shaft is not firm and unstable, and the production cost is high and the w

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Powder metallurgy passenger car chain pulley and method for producing the same
  • Powder metallurgy passenger car chain pulley and method for producing the same
  • Powder metallurgy passenger car chain pulley and method for producing the same

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0031] Example 1

[0032] As attached figure 1 , 2 , 3, 4, 5 produce powder metallurgy car sprockets, the production steps are as follows:

[0033] (1) Selection of ingredients and raw materials:

[0034] The sprocket body and teeth are made of powder metallurgical raw materials, and the weight percentage of each raw material is: copper powder accounts for 3%, nickel powder accounts for 2%, graphite powder accounts for 0.6%, molybdenum powder accounts for 1.5%, and iron powder accounts for 92.9%; The oil ring 7 is made of GCr15 steel; the sealing ring 8 is made of high-quality carbon steel;

[0035] (2) Mixed powder:

[0036] The copper powder, nickel powder, graphite powder, molybdenum powder, and iron powder weighed according to the above weight ratio are uniformly mixed by a double cone mixer, and the powder mixing time is 60 minutes, which is used as the powder metallurgical mixing of the pressed gear body and teeth Powder

[0037] (3) Suppression:

[0038] Put the powder met...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Heightaaaaaaaaaa
Diameteraaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a powder metallurgy cab chain wheel and a preparation method, which is composed of a chain wheel body (1), teeth (2), characterized in that, the chain wheel body (1) arranges a locking D-shape shaft hole (4) at the center of the ring boss (3), a central circular shaft hole (6) is arranged at the center of the ring boss (3') of the other side, a flinger (7) is arranged on the outside of the perinium of the ring boss (3, 3'), and the surface is welded with a sealing ring (8). The preparation method is to adopt the powder metallurgy materials for once sintering into an integer. The powder metallurgy cab chain wheel of the preparation method has the advantages of abrasion proof, corrosion resistant, good integrity, also has easy installment, fixation, light proportion, high precision, easy mass production, moreover the device has excellent lubricating property, especially for the chain wheel of the cab.

Description

technical field [0001] The invention relates to a car sprocket and a preparation method thereof, in particular to a powder metallurgy car sprocket and a preparation method thereof. Background technique [0002] Because powder metallurgy sintered products have the advantages of corrosion resistance, wear resistance, high precision, high strength, low production cost, easy mass production, and good integrity, they are widely used. However, due to the particularity of the powder metallurgy product process, the matrix has many gaps, and cracks are prone to occur during quenching, especially at the root of the tooth, so processing is difficult. However, after searching, the sprockets currently used in cars are still steel machined products, and there is no report of using powder metallurgy to prepare sprockets for cars. Its structure is composed of sprocket body, teeth and shaft holes, and the shaft holes are round. Shape, the sprocket body is a whole piece. The shortcomings of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): F16H55/30F16H55/06B22F5/08
Inventor 吕元之张应波吴兆花吴荣昌童民
Owner 吕元之
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap