Preparation method for full-body polished porcelain tiles

A production method and technology of sapphire bricks, applied in the production field of ceramic tiles, can solve the problems of low strength, low water absorption, poor architectural decoration performance, etc., and achieve the effects of unchanged physical and chemical properties, improved coloring concentration, and long service life.

Inactive Publication Date: 2008-10-15
关锐华
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, most of the common porcelain tiles on the market have problems such as high water absorption, poor anti-skid effect, low strength, poor anti-fouling effect, monotonous designs and varieties, and poor architectural decoration performance. High-efficiency, high-strength, strong anti-fouling performance, rich and colorful porcelain antique bricks

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0026] A kind of production method of porcelain quality full-body polished goldstone brick of the present invention, comprises the following steps:

[0027] (1) Adobes for the manufacture of kampizite bricks:

[0028] ①According to the weight percentage of the powder: 69-73% of silicon dioxide, 16-20% of alumina, 2.2-3.8% of potassium monoxide, 2.2-4.5% of disodium oxide, 0.5-1% of Iron trioxide, 0.005-0.25% titanium oxide, 0.12-0.6% calcium oxide and 0.6-1.2% magnesium oxide, and mix the obtained powders evenly to obtain the required mixed powder;

[0029] ② Put the mixed powder into the ball milling equipment and ball mill it into a slurry. The ball milling time is 12-13 hours. The slurry concentration requirement: the water content should be controlled at 30-32%. After sieving, put it into the pulp tank, and finally get the pulp that meets the requirements;

[0030] ③ Add appropriate amount of coloring material as required, and mix the coloring material and slurry evenly;...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for manufacturing porcelain full-body polished King Beige tiles, which mainly comprises the following steps: firstly, green bricks of the King Beige tiles are manufactured; and secondly, glaze is applied to the surfaces of the finished green bricks, wherein, the manufacture of the green bricks of glazed tiles and the King Beige tiles further comprises the following steps: raw material selecting, slurry preparing, color matching, drying, powder making, green brick pressing, green brick drying, etc., and the step of applying the glaze to the surfaces of the finished green bricks mainly comprises the following procedures: the glaze slurry is prepared, the glaze slurry is applied, glazed tile products, etc. are sintered, etc. The method has the advantages of extremely low water absorption rate, high strength, good anti-skid and anti-fouling effects, good durability, etc., and is widely applicable to the decorative walls or floors of advanced hotels, grand and large-scale activity places, airports, homes, etc.

Description

technical field [0001] The invention relates to a method for producing tiles. Background technique [0002] There are many types of porcelain tiles, and various porcelain tiles for different purposes can be produced by different composition ratios and different processes. However, most of the common porcelain tiles on the market have problems such as high water absorption, poor anti-skid effect, low strength, poor anti-fouling effect, monotonous designs and varieties, and poor architectural decoration performance. High-efficiency, high-strength, strong anti-fouling performance, rich and colorful porcelain antique bricks. Contents of the invention [0003] The object of the present invention is to provide a production method of porcelain whole body polished kilapis brick with extremely low water absorption, high strength, good antifouling effect and good durability. [0004] Technical scheme of the present invention is realized like this: [0005] A kind of production me...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B35/14C04B35/622C04B41/86
Inventor 关锐华
Owner 关锐华
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com