Process for producing twin crystal inducement plastic steel material with high carbon content

A technology of twinning induced plasticity and iron and steel materials, applied in metal rolling, manufacturing tools, temperature control, etc., can solve the problems of limited application range, low material performance, etc., achieve low cost, simple preparation method, and good application prospects Effect

Inactive Publication Date: 2009-05-13
UNIV OF SCI & TECH BEIJING
View PDF3 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This method is a method of continuous production of thin strips using special equipment, it

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Process for producing twin crystal inducement plastic steel material with high carbon content
  • Process for producing twin crystal inducement plastic steel material with high carbon content
  • Process for producing twin crystal inducement plastic steel material with high carbon content

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The steel plate is prepared by traditional vacuum smelting and hot rolling process

[0027] Its composition is: C%=0.63wt%, Mn%=23.6wt%, Si%=0.20wt%, P%=0.009wt%, S%=0.0065wt%, Al%=0.036wt%, the balance is Fe .

[0028] Smelting process: Vacuum smelting in an electromagnetic induction furnace, filled with argon for protection, and cast into a 90mm slab.

[0029] Rolling process: the heating temperature of the steel material is 1200°C, and the heat preservation is 3 hours for homogenization treatment. Hot rolled on a 350 two-roll hot rolling mill to obtain a hot-rolled sheet with a thickness of about 3.5mm and a total deformation of 95%. / s), can obtain tensile strength 1001MPa, yield strength 535MPa, while elongation reaches 52% hot-rolled sheet.

Embodiment 2

[0031] Steel plates are prepared by traditional vacuum smelting and hot rolling and cold rolling processes

[0032] Smelting process: Vacuum smelting in an electromagnetic induction furnace, filled with argon for protection.

[0033]Rolling process: The heating temperature of the steel material is 1200℃, and the temperature is kept for 3 hours for homogenization treatment. Hot-rolled on a 350 two-high hot rolling mill to obtain a hot-rolled sheet with a thickness of about 3 mm, the total deformation is 95%, and the opening and final rolling temperatures are 1100 ° C and 950 ° C, respectively, and cooled on a 430 four-high cold rolling mill. The test sheet was rolled and cold rolled to a thickness of 1.0 mm, and the cold rolling reduction ratio was 66.7%.

[0034] Heat treatment process: 1.0mm thick cold-rolled steel sheet is kept in a heating furnace at 700°C for 20 minutes, and then cooled to room temperature at a rate of 10°C / s.

[0035] The optical microstructure observed...

Embodiment 4

[0041] The difference from Example 1 and Example 2 is that the composition of the steel material is: C%=0.44wt%, Mn%=21.44wt%, Si%=0.10wt%, P%=0.006wt%, S% =0.0055wt%,Al%=0.026wt%,

[0042] The balance is Fe. 经过实施例1和例2的加工过程,

[0043] The cold rolling reduction rate is 71.4%, the thickness of the cold rolling sheet is 1.06mm, the heat treatment temperature is 750°C, the temperature is kept for 15 minutes, and the temperature is cooled to room temperature at a rate of 30°C / s.

[0044] A high-strength and high-plastic twin-induced plasticity steel was prepared under this process condition. The steel material also has a microstructure of annealing twins and stacking faults in the austenite matrix as observed by transmission electron microscopy, and its grain size is 2-5 μm. . The yield strength of the steel material at room temperature is 465MPa, the tensile strength is 1040MPa, and the elongation is 61.0%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Yield strengthaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the field of preparing a steel material and in particular relates to a method for preparing a twin crystal induced plastic steel material with high carbon content. The twin crystal induced plastic steel material comprises the following compositions in the range: 0.2 to 0.49weight percent or 0.55 to 1.5weight percent of C, 10 to 22weight percent or 23.1 to 35weight percent of Mn, less than 1weight percent of Al, less than 1weight percent of Si, less than 0.008 percent of S, less than 0.02 percent of P and the balance being Fe and inevitable impurities. The preparation method comprises the following steps: a plate blank prepared through smelting is subjected to a hot rolling process to obtain a hot rolled sheet in a use state; or the plate blank is subjected to hot rolling and cold rolling to obtain a cold rolled sheet; the sheet is subjected to heat treatment in order that the tensile strength is between 750 and 1,200 MPa, the yield strength is between 230 and 615 MPa, the extension rate is between 45 and 70 percent; and no tough brittle turning point exists at a temperature of more than 100 DEG C. The steel material with high strength and high plasticity has excellent comprehensive mechanical performance, machining performance and forming performance, can be used for a steel rail of a railroad, automobile manufacture, engineering machinery, an oil and gas transportation pipeline, a liquefied natural gas transportation ship, war industry and other industries and has important value and great application space for an automobile industry and a war industry with rapid development.

Description

technical field [0001] The invention belongs to the field of iron and steel material preparation, and relates to a method for preparing a twin-induced plastic iron and steel material with high carbon content. Background technique [0002] In the 21st century, the rapid development of light-weight and energy-saving vehicles, deep well oil production pipes and large-diameter oil (gas) pipes, large-scale construction machinery, long-span heavy-duty bridges, large-scale high-performance ships and high-rise buildings, etc., is especially important for my country's key development The basic railway transportation business puts forward higher requirements on the performance and service life of steel materials. At the same time, the competition in the steel industry is escalating day by day, and the requirements of users are also constantly improving. All these problems are posing serious challenges to the sustainable and stable development of the steel industry. Therefore, relying...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C21D8/02C22C38/06B21B37/74B21B37/16C21D9/52
Inventor 米振莉唐荻江海涛代永娟吕建崇
Owner UNIV OF SCI & TECH BEIJING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap