Preparation method of carbide-Co/Ni composite powder and hard alloy

A cemented carbide and composite powder technology, applied in the fields of hydrometallurgy and powder metallurgy, can solve the problems of excessive WC particle breakage, etc., and achieve the effect of short process, low cost and less emission

Inactive Publication Date: 2009-08-19
CENT SOUTH UNIV +1
View PDF0 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] In order to avoid the problem of excessive breakage of WC particles caused by the wet grinding process and solve the problem of preparing coarse-grained, ultra-coarse-grained, and extra-coarse-grained hard alloys, the present

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of carbide-Co/Ni composite powder and hard alloy
  • Preparation method of carbide-Co/Ni composite powder and hard alloy
  • Preparation method of carbide-Co/Ni composite powder and hard alloy

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Example 1 WC-Co-Ni composite powder was prepared according to the composition of WC-6.25wt.%Co-6.25wt.%Ni. WC with a FSSS of 6.5 μm was selected as the raw material, and the mechanical pretreatment was carried out by ball milling in a ball mill for 6 hours at a ball-to-material ratio of 3:1. 200g NH 4 Cl and 53.82g CoCl 2 ·6H 2 O, 53.95g NiCl 2 ·6H 2 O was dissolved in deionized water respectively; the two were mixed and filtered; 64.73 g concentrated NH was added 3 Water, configure 1L cobalt ammonia complex solution. 200 g of the above-mentioned WC powder and the above-mentioned cobalt-ammonia complex solution were put into a 2L autoclave. with N 2 After exhausting the air in the kettle, pass in H 2Make the pressure in the kettle reach 3.5MPa, adjust the rotation speed of the autoclave to 1000r / min, keep the temperature at 170°C, and keep the temperature at 3h to carry out the hydrothermal high-pressure hydrogen reduction reaction. After the reaction, the obta...

Embodiment 2

[0025] Example 2 WC-Co composite powder was prepared according to WC-12.5wt.% Co composition. WC with a FSSS of 6.5 μm was selected as the raw material, and the mechanical pretreatment was carried out by ball milling in a ball mill for 6 hours at a ball-to-material ratio of 3:1. 250g (NH 4 ) 2 SO 4 with 136.24g CoSO 4 ·7H 2 O was dissolved in deionized water respectively; the two were mixed and filtered; 64.73 g concentrated NH was added 3 water (NH 3 :Co=2.2:1), configure 1L cobalt ammonia complex solution. 200 g of the above-mentioned WC powder and the above-mentioned cobalt-ammonia complex solution were put into a 2L autoclave. with N 2 After exhausting the air in the kettle, pass in H 2 Make the pressure in the kettle reach 3.5MPa, adjust the rotation speed of the autoclave to 1000r / min, keep the temperature at 170°C, and keep the temperature at 3h to carry out the hydrothermal high-pressure hydrogen reduction reaction. After the reaction was completed, the WC-Co...

Embodiment 3

[0026] Example 3 WC-Co composite powder was prepared according to the WC-8wt.% Co composition. Select WC with FSSS of 12.0 μm as raw material, and perform mechanical pretreatment by ball milling in a ball mill for 8 hours at a ball-to-material ratio of 3:1. 150gNH 4 Cl and 70.18g CoCl 2 ·6H 2 O was dissolved in deionized water respectively; the two were mixed and filtered; 39.40 g concentrated NH was added 3 water (NH 3 :Co=2.2:1), configure 1L cobalt ammonia complex solution. 200 g of the above-mentioned WC powder and the above-mentioned cobalt-ammonia complex solution were put into a 2L autoclave. The rest of the process parameters are the same as in Example 2. The results of chemical analysis showed that the Co content in the WC-Co composite powder was 7.41wt.%, the O content (total oxygen analysis) was 0.1091wt.%, the H content was 0.0104wt.%, and the Co yield was 92.6%. The combination of the metallographic observation of the polished section of the alloy shows tha...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for preparing carbide (MC)-Co/Ni composite powder and hard alloy, and belongs to the field of wet metallurgy and powder metallurgy. The method adopts mechanically pretreated MC powder using WC as a main component and cobalt/nickel ammine complexing solution as raw materials, utilizes the self-catalysis activity of the mechanically pretreated MC powder, and adopts a hydrothermal high-pressure hydrogen reduction process to prepare the MC-Co/Ni composite powder under the condition that a sensitizing agent, an activating agent and a catalyst are not added; and on the basis, the method prepares the hard alloy of which the grain size is more than or equal to 4.5mu m without a wet grinding process. The method has the characteristics of low cost, short flow and high purity, does not cause alloy pollution, and the like.

Description

technical field [0001] The invention relates to a hydrometallurgical preparation method of carbide (MC)-Co / Ni composite powder for cemented carbide production and the preparation of coarse-grained, ultra-coarse-grained and extra-coarse-grained with grain size ≥ 4.5 μm using it as a raw material The preparation method of cemented carbide belongs to the field of hydrometallurgy and powder metallurgy. Background technique [0002] According to the classification standard of cemented carbide by Sandvik, the largest cemented carbide manufacturer in the world, the cemented carbides with WC grain size of 3.5-4.9 μm, 5.0-7.9 μm and 8.0-14 μm are respectively coarse-grained, super-sized Coarse-grained and extra-coarse-grained cemented carbide. Ultra-coarse and extra-coarse-grained cemented carbide is currently a domestic blank. Under the condition of the same Co content, compared with the traditional medium and coarse grained cemented carbide, the ultra-coarse and extra-coarse grai...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B22F9/00B22F9/04B22F9/26C22C1/05C22C29/08
Inventor 张立吴厚平陈青林
Owner CENT SOUTH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap