Environmental-friendly type foamless anti-staining detergent, preparing method and application thereof
A cleaning agent and anti-fouling technology, applied in detergent compositions, chemical instruments and methods, non-surface-active detergent compositions, etc., can solve the problems of not easy biodegradation, unfavorable environment, etc., and improve color fastness. , good cleaning effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0083] Example 1:
[0084] 1. Preparation of copolymer:
[0085] A. Preparation of the initiator aqueous solution: 1.5 grams of potassium persulfate and 20 grams of water are added to make the initiator aqueous solution;
[0086] B. Synthesis of copolymer: Add 3.5g of N-vinylpyrrolidone, 7.2g of maleic anhydride, 5.0g of itaconic acid, 22g of acrylamide, 50g of water, 6.1g of acrylic acid and 1.5g of methacrylic acid into a 500ml four-necked flask. , Warm up to 50-70℃, keep for 30-60 minutes to fully dissolve the raw materials, add 1.2g sodium bisulfite and 7g initiator aqueous solution, the reactant will naturally rise to 70-90℃, maintain 80-90℃ slowly respectively Add the remaining potassium persulfate aqueous solution and the remaining mixture of 10 g of acrylic acid, 2 g of methacrylic acid and 50 g of water. After the addition, the reactant is heated to 80-100°C for 3-5 hours; after the reaction is completed, the temperature is lowered to below 40°C, Adjust the pH value of th...
Example Embodiment
[0091] Example 2:
[0092] The preparation process of the copolymer, the phosphorus-free alkali-resistant high-efficiency chelating dispersion stabilizer, and the environmentally-friendly non-foaming anti-staining detergent are the same as in Example 1, and their respective compositions are as follows:
[0093] A. Initiator aqueous solution: potassium persulfate 4.8g, water 20g;
[0094] B. Synthesis of copolymer: Add 5.0g of N-vinylpyrrolidone, 6.6g of maleic anhydride, 4.8g of itaconic acid, 18.8g of acrylamide, 50g of water, 5.8g of acrylic acid and methacrylic acid into a 500ml four-necked flask. 0g, warm up to 55-70°C, keep for 30-60 minutes to fully dissolve the raw materials, add 1.5g sodium bisulfite and 7g initiator aqueous solution, the reactant will naturally heat up to 70-90°C and maintain 80-90°C slowly Add the remaining potassium persulfate aqueous solution and the remaining mixture of acrylic acid 10g, methacrylic acid 0g and water 50g respectively. After the additi...
Example Embodiment
[0097] Example 3:
[0098] The preparation process of the copolymer, the phosphorus-free alkali-resistant high-efficiency chelating dispersion stabilizer, and the environmentally-friendly non-foaming anti-staining detergent are the same as in Example 1, and their respective compositions are as follows:
[0099] A. Initiator aqueous solution: 3.5g potassium persulfate, 20g water;
[0100] B. Synthesis of copolymer: Add 6.0g of N-vinylpyrrolidone, 9.0g of maleic anhydride, 5.5g of itaconic acid, 15.0g of acrylamide, 50g of water, 4g of acrylic acid and 2g of methacrylic acid into a 500ml four-necked flask. , Warm up to 55-65°C, keep for 30-60 minutes to fully dissolve the raw materials, add 3.0g sodium bisulfite and 7g initiator aqueous solution, the reactant will naturally rise to 70-90°C, maintain 80-90°C slowly respectively Add the remaining potassium persulfate aqueous solution and the remaining mixture of 10.0g of acrylic acid, 2g of methacrylic acid and 50g of water. After the...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap