Low chromium anticorrosive chemical conversion treating fluid on surface of constructive aluminium profile and use method thereof

A chemical conversion treatment and conversion treatment technology, applied in the field of chemical conversion film treatment on the surface of aluminum alloys, can solve the problems of high waste water treatment cost, poor stability of chromating solution, easy ash on the surface of workpieces, etc. Bright and beautiful effect

Inactive Publication Date: 2009-12-09
佛山科富科技有限公司
View PDF0 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In recent years, China has begun to study chromate conversion treatment technology, and has successively developed some chromate conversion treatment solutions, but at present, potassium ferricyanide is generally used as an accelerator, and ferricyanide will be catalyzed by ultraviolet light and decomposed into toxic cyanide. At the same time, there ar

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] Put the architectural aluminum profiles after acid-etching and degreasing treatment in chromate containing 1.0 g / L, fluorine compound 0.5 g / L, zinc salt 0.4 g / L, nitrate 0.8 g / L, rare earth metal salt 0.2 g / L , Stabilizer 0.3 g / L, PH value 1.8-2.2, temperature 5-40 ℃ bath treatment, treatment time 3-5 minutes (dipping) or 0.5-1.5 minutes (spraying), can be in the building aluminum profile A dense and uniform layer is formed on the surface, and the film weight per unit area is 0.2-1.3g / m 2 , Golden yellow to iridescent chromate conversion coating with a film thickness of 1-2 μm, the salt spray test exceeds the national standard of 168 hours, strong corrosion resistance, good bonding with organic coatings, adhesion, impact strength, cupping Various performance indicators such as tests have reached the national standard.

Embodiment 2

[0037] Put the architectural aluminum profiles after acid-etching and degreasing treatment in 2.0 g / L chromate, 0.3 g / L fluorine compound, 0.1 g / L zinc salt, 0.4 g / L nitrate, and 0.5 g / L rare earth metal salt. , Stabilizer 0.8 g / L, PH value 1.8-2.2, temperature 5-40 ℃ bath treatment, treatment time 3-5 minutes (dipping) or 0.5-1.5 minutes (spraying), it can be used in building aluminum profiles A dense and uniform layer is formed on the surface, and the film weight per unit area is 0.2-1.3g / m 2 , Golden yellow to iridescent chromate conversion coating with a film thickness of 1-2 μm, the salt spray test exceeds the national standard of 168 hours, strong corrosion resistance, good bonding with organic coatings, adhesion, impact strength, cupping Various performance indicators such as tests have reached the national standard.

Embodiment 3

[0039] Put the architectural aluminum profiles after acid-etching and degreasing treatment in 0.6 g / L chromate, 0.9 g / L fluorine compound, 0.3 g / L zinc salt, 0.2 g / L nitrate, and 0.3 g / L rare earth metal salt. , Stabilizer 0.5 g / L, PH value 1.8-2.2, temperature 5-40 ℃ bath treatment, treatment time 3-5 minutes (dipping) or 0.5-1.5 minutes (spraying), it can be used in building aluminum profiles A dense and uniform layer is formed on the surface, and the film weight per unit area is 0.2-1.3g / m 2 , Golden yellow to iridescent chromate conversion coating with a film thickness of 1-2 μm, the salt spray test exceeds the national standard of 168 hours, strong corrosion resistance, good bonding with organic coatings, adhesion, impact strength, cupping Various performance indicators such as tests have reached the national standard.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a low chromium anticorrosive chemical conversion treating fluid on the surface of constructive aluminium profile and a use method thereof; the technology comprises placing constructive aluminium profile in a tank liquor to treat with a pH value of 1.8-2.2 at 5-40 DEG C for 3-5min or 0.5-1.5min to form a layer of compact and uniform golden to irisated chromate conversion film with a film thickness of 1-2mu m on the surface of the constructive aluminium profile; wherein, the tank liquor comprises 0.6-2.0g/L of chromate, 0.3-0.9g/L of fluorine compound, 0.1-0.6g/L of zinc salt, 0.2-0.8g/L of nitrate, 0.1-0.5g/L of salts from rare earth metals and 0.3-1.0g/L of stabilizer. The invention has simple process and contains no potassium ferricyanide and low chromate; the solution is stable with little sediment; the service cycle is long; the cost of environment pollution and wastewater treatment is low; the treated waste solution can meet the relative discharge standards and the invention has other advantages of room temperature use, energy saving, low comprehensive cost and the like.

Description

Technical field: [0001] The invention relates to the technical field of chemical conversion film treatment on the surface of aluminum alloys, in particular to a low-chromium anti-corrosion chemical conversion treatment liquid on the surface of building aluminum profiles and a method for using the same. Background technique: [0002] Aluminum alloy profiles for construction require high comprehensive performance such as corrosion resistance, weather resistance, wear resistance, good appearance decoration and long service life. Therefore, aluminum profiles are protected by electrostatic powder spraying and fluorocarbon resin paint coating. Before decoration, surface chemical conversion treatment must be carried out to improve the bonding force between the coating and the substrate and meet the high corrosion resistance requirements. At present, chromate conversion treatment is basically used in my country. Some countries in Europe and the United States have introduced chromate-...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23C22/37C23C22/38
Inventor 袁兴蒙文坚王运玖
Owner 佛山科富科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap