Mending paste special for lost foam casting

A technology of lost foam casting and repair paste, which is applied in the direction of casting and molding equipment, etc. It can solve the problems of poor quality of castings, high pyrolysis residues, and low strength of repair paste, so as to solve wrinkled skin defects and improve competitiveness. ability, good surface finish effect

Inactive Publication Date: 2010-02-10
郑宝安
View PDF0 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The currently used repair paste has low strength, poor moldability, large gas generat

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] A special repair paste for lost foam casting is characterized in that its components and weight content are as follows:

[0011] Stearic acid 800g, paraffin wax 200g, polyethylene glycol 150g, sodium hydroxide 50g, water 400g. Wherein the melting point of stearic acid is 70-71° C., the freezing point is 54-57° C., the viscosity of polyethylene glycol is 37-45 Pa.s, and the hydroxyl value is 268-249 mgHON / g.

Embodiment 2

[0013] A special repair paste for lost foam casting is characterized in that its components and weight content are as follows:

[0014] Stearic acid 700g, paraffin 300g, polyethylene glycol 200g, sodium hydroxide 40g, water 500g. Wherein the melting point of stearic acid is 70-71° C., the freezing point is 54-57° C., the viscosity of polyethylene glycol is 37-45 Pa.s, and the hydroxyl value is 268-249 mgHON / g.

Embodiment 3

[0016] A special repair paste for lost foam casting is characterized in that its components and weight content are as follows:

[0017] Stearic acid 750g, paraffin wax 250g, polyethylene glycol 100g, sodium hydroxide 45g, water 450g. Wherein the melting point of stearic acid is 70-71° C., the freezing point is 54-57° C., the viscosity of polyethylene glycol is 37-45 Pa.s, and the hydroxyl value is 268-249 mgHON / g.

[0018] The preparation method of the above-mentioned special repairing paste for lost foam casting: mix stearic acid, paraffin, polyethylene glycol, and water into a steel vessel, then heat, add sodium hydrogenation after the stearic acid and paraffin are completely dissolved, and stir Let stand to room temperature to form.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Melting pointaaaaaaaaaa
Freezing pointaaaaaaaaaa
Viscosityaaaaaaaaaa
Login to view more

Abstract

The invention relates to a mending paste special for lost foam casting, comprising the following components in parts by weight: 70-80 parts of stearic acid, 20-30 parts of paraffin, 10-20 parts of polyethylene glycol, 4-5 parts of sodium hydroxide and 40-50 parts of water, wherein the melting point of stearic acid is 70-71 DEG C, the freezing point is 54-57 DEG C, the viscosity of polyethylene glycol is 37-45Pa-s and the hydroxyl value is 268-249mgHON/g. The mending paste has the advantage of good forming property and levelling property, high strength, good surface glossiness, low gas generation and good residue decomposition property at high temperature.

Description

technical field [0001] The invention belongs to a chemical product, in particular to a special repair paste for lost foam casting. Background technique [0002] Lost foam casting is a casting process in which polystyrene is used to make a foam model. Under negative pressure, molten iron is used to vaporize the foam model and replace the space occupied by the foam model, and then cooled to form a casting. Because foam models tend to be scrapped due to defects such as poor surface fusion during the manufacturing process, a layer of repair paste is usually applied to the defective surface to repair the defects. The repair paste currently used has low strength, poor moldability, large gas generation, and many pyrolysis residues, so the quality of the casting cannot be well guaranteed. Contents of the invention [0003] The technical problem to be solved by the present invention is to overcome the deficiencies and shortcomings of the above-mentioned prior art, and provide a sp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B22C7/02
Inventor 郑宝安
Owner 郑宝安
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap