Waterborne PU high smooth wax resin for synthetic leather

A synthetic leather and resin technology, applied in fiber types, textiles and papermaking, fiber processing, etc., can solve the problems of poor synthetic leather viscosity, stability, hand feel and other comprehensive effects, synthetic leather bottom layer dissolution, synthetic leather feel bad and other problems, to achieve the effect of excellent comprehensive effect, solvent resistance of coating and full hand feeling.

Inactive Publication Date: 2010-02-17
JIANGSU BAOZE POLYMER MATERIAL
View PDF0 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] 1. The organic solvent contained in the solvent-based wax resin will cause the bottom layer of synthetic leather or artificial leather to dissolve, and the treated synthetic leather will not feel good;
[0005] 2. The organic solvent contained in solvent-based wax resin not only has high cost, strong odor, and is easy to pollute the environment, but also has safety hazards such as flammability and explosion;
[0006] 3. Synthetic leather products prepared by solvent-based wax resins have poor comprehensive effects such as viscosity, stability, and hand feel.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] 1. The water-based PU high-smooth wax resin for synthetic leather is composed of the following raw materials: 40 kg of water-based polyurethane resin (30% solid content), 30 kg of water-based fluorosilicone resin, 20 kg of ordinary tap water, 0.5 kg of water-based wax emulsion, and smooth silicone oil 3 kg of agent, 5 kg of silicone defoamer, 3 kg of silicone leveling agent and 3 kg of water-based polyurethane thickener.

[0029] 2. The preparation method of the water-based PU high smooth wax resin for synthetic leather of the present invention is as follows:

[0030] ①According to the above ratio, select 40 kg of water-based polyurethane resin (30% solid content), 30 kg of water-based fluorosilicone resin, 20 kg of ordinary tap water, 0.5 kg of water-based wax emulsion, 3 kg of silicone oil slip agent, and 5 kg of silicone defoamer , 3 kg of silicone leveling agent, stirred for 2 hours, fully mixed, set aside;

[0031] ② Grinding and filtering the reaction mixture obt...

Embodiment 2

[0037] 1. The water-based PU high-smooth wax resin for synthetic leather is composed of the following raw materials: 40 kg of water-based fluorosilicone resin, 30 kg of aliphatic polyurethane emulsion (30% solid content), 30 kg of ordinary tap water, 0.8 kg of water-based wax emulsion, silicone grease 3 kg of cool agent, 5 kg of silicone defoamer, 1 kg of silicone leveling agent and 2 kg of water-based polyurethane thickener.

[0038] 2. The preparation method of the water-based PU high smooth wax resin for synthetic leather of the present invention is as follows:

[0039] ① Select 40 kg of water-based fluorosilicone resin according to the above ratio, 30 kg of aliphatic polyurethane emulsion (30% solid content), 30 kg of ordinary tap water, 0.8 kg of water-based wax emulsion, 3 kg of silicone oil slip agent, and 5 kg of silicone defoamer kg, 1 kg of silicone leveling agent, stirred for 2 hours, fully mixed, and set aside;

[0040] ② Grinding and filtering the reaction mixtur...

Embodiment 3

[0046] 1. The water-based PU high-smooth wax resin for synthetic leather is composed of the following raw materials: 30 kg of water-based fluorosilicone resin, 20 kg of aliphatic polyurethane dispersion (30% solid content), 15 kg of ordinary tap water, 0.3 kg of water-based wax emulsion, organic silicone oil 1.5 kg of slip agent, 2 kg of silicone defoamer, 0.5 kg of silicone leveling agent and 1 kg of non-ionic polyurethane polymer.

[0047] 2. The preparation method of the water-based PU high smooth wax resin for synthetic leather of the present invention is as follows:

[0048] ① Select 30 kg of water-based fluorosilicone resin according to the above proportions, 20 kg of aliphatic polyurethane emulsion (30% solid content), 15 kg of ordinary tap water, 0.3 kg of water-based wax emulsion, 1.5 kg of silicone oil slip agent, and 2 kg of silicone defoamer kg, 0.5 kg of silicone leveling agent, stirred for 2 hours, fully mixed, and set aside;

[0049] ② Grinding and filtering th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a waterborne PU high smooth wax resin for synthetic leather and the resin comprises the following raw materials by weight percent: 30-40% of waterborne silicon-fluorine resin,20-30% of waterborne polyurethane, 10-30% of water, 0.2-0.8% of waterborne wax emulsion, 1-3% of organic silicone oil smoothing agent, 0.5-1% of organic silicone flatting agent, 2-5% of organic silicone defoamer and 0.5-2% of waterborne polyurethane thickener. The waterborne PU high smooth wax resin for synthetic leather provided by the invention uses water as solvent instead of toxic solvents such as dimethyl formamide, butanone and the like and has the advantage of noninflammability, safety, environmental protection, cost-saving and the like. The finished product prepared from the waterbornePU high smooth wax resin for synthetic leather provided by the invention has full hand feeling, high luster and high luminance, extremely smooth waxy feeling, delicate texture and good air permeability; and the prepared synthetic leather has good comprehensive effect in hand feeling, smoothness, water resistance, waxy feeling and the like.

Description

technical field [0001] The invention relates to a wax resin for synthetic leather, in particular to a water-based PU high-smooth wax resin for synthetic leather used in the front-end process of synthetic leather. Background technique [0002] At present, synthetic leather products have gradually become a popular trend in the future, and synthetic leather has been widely used in the production of luggage, clothing, footwear and other products. The base fabric of PU leather is a canvas PU material with good tensile strength. In addition to being coated on the top of the base fabric, the base fabric can also be included in the middle, so that the existence of the base fabric cannot be seen from the outside. PU leather has physical properties. Good, resistance to twists and turns, good softness, high tensile strength, and breathability, so PU leather is widely used in the fabric of footwear or the weight-bearing parts of bags. [0003] At present, the wax resins for synthetic l...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/657D06M15/564D06M13/224D06N3/12D06M101/30
Inventor 时云刚
Owner JIANGSU BAOZE POLYMER MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap