Composite printing paste and preparation method thereof

A printing paste and raw material technology, applied in the field of textile printing and dyeing, can solve the problems of high production cost, high cost, resource limitation, etc., and achieve the effect of low production cost, low consumption and high color fastness

Inactive Publication Date: 2010-03-31
LOFTEX INDS
View PDF0 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, since the main raw material for preparing sodium alginate is kelp, not only the resources are limited, but also the cost is high. The price of each ton of sodium alginate dry powder is about 40,000 yuan, and each ton of dry powder can be prepared with 10 tons of printing paste, which is used in the printing and dyeing industry. The cost per ton of color paste is about 4,000 yuan, and the production cost is very high
In addition, the stability period of sodium alginate slurry is too short when used, and the slurry can only be stored for 2 days at room temperature. It needs to be printed and used immediately under high temperature in summer, which is inconvenient and easy to cause waste

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Take the preparation of 1000 liters of printing paste as an example.

[0028] (1), technology described in the present invention:

[0029] A composite printing paste, the components and their weights in the raw material composition are: modified carboxymethyl cellulose 14.5kg; anti-staining salt 4.5kg; hexabia 1kg; baking soda 40kg; urea 80kg; 50L; the remainder is water.

[0030] The preparation method of above-mentioned compound printing paste, comprises the following steps:

[0031] (1) Take materials according to the formula ratio;

[0032] (2), under normal temperature, add 500 liters of water in 1000 liters of containers;

[0033] (3) Turn on the low-speed agitator at 750 rpm, constant speed; add hexabia, and after it is fully dissolved and the water quality softens, add 100 liters of anti-staining salt with a concentration of 45 g / L dissolved in 55 °C water, and stir 4 minutes; add urea and stir for 4 minutes;

[0034] (4), turn off the low speed of 750 rpm,...

Embodiment 2

[0040] Take the preparation of 1000 liters of printing paste as an example.

[0041] (1), technology described in the present invention:

[0042] A composite printing paste, the components and their weights in the raw material composition are: modified carboxymethyl cellulose 15.5kg; anti-staining salt 6.5kg; hexabia 2kg; baking soda 50kg; urea 90kg; 60L; the remainder is water.

[0043] The preparation method of above-mentioned compound printing paste, comprises the following steps:

[0044] (1) Take materials according to the formula ratio;

[0045] (2), under normal temperature, add 500 liters of water in 1000 liters of containers;

[0046] (3) Turn on the low-speed agitator at 700 rpm and constant speed, add 2kg of hexabia one by one, fully dissolve and soften the water, then dissolve 6.5kg of anti-staining salt with 100 liters of 50℃ water, then directly add 1000 liters In the container, stir for 5 minutes, then add 90kg of urea, and stir in the container for 5 minute...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of textile printing and dying, in particular to a composite printing paste and a preparation method thereof. The raw material of the composite printing paste comprises the following components in percentage by weight: 1.45-1.55 percent of modified carboxymethylcellulose, 0.45-0.65 percent of dying resistant salt, 0.1-0.2 percent of sodium hexametaphosphate, 4-5 percent of sodium bicarbonate, 8-9 percent of urea, 5-6 percent of 909 thickening agent and the balance of water. The water is added at normal temperature to be uniformly stirred for later use. When used as active dye printing paste, the invention has high tinctorial yield, saves dye and is excellent novel composite printing paste.

Description

technical field [0001] The invention relates to the technical field of textile printing and dyeing, in particular to a composite printing paste and a preparation method thereof. Background technique [0002] Printing paste refers to the substance added to the printing paste to thicken. Generally, it can be dissolved in water or fully swelled and dispersed in water to form a thick colloidal solution. When preparing printing paste, part of the dye is dissolved in water, and another part of the dye is dissolved, adsorbed or dispersed in the printing paste, that is, the paste acts as a carrier for the paste. Whether the physical and chemical properties of the paste used to prepare the color paste are appropriate will directly affect the printing quality of the printed product, such as the vividness of the color, the clarity and penetration of the pattern outline, and the technical indicators such as the ease of washing after printing. Therefore, printing paste occupies an impor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06P1/50
Inventor 王红星
Owner LOFTEX INDS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products