Manufacturing method of strong twinkling aluminium pastes

A manufacturing method and technology of aluminum silver paste, applied in the directions of pigment paste, dyeing physical treatment, fibrous filler, etc., can solve the problems of wide particle size distribution, irregular particle shape, poor scintillation performance, etc., and achieve narrow particle size distribution, surface Smooth and clean, strong flickering performance

Active Publication Date: 2010-06-16
长沙族兴新材料股份有限公司
View PDF0 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But this method is to use large steel balls to break the coarse aluminum powder into scales, the shape of the product particles is irregular, the surface smoothn

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0012] Example 1:

[0013] (1) In the φ800×1000 vertical stirring ball mill, 500kg of glass balls with a diameter of 1.0-5.0mm are loaded, and 100kg of D50 solvent oil is added, D 50 7.8μm nitrogen atomized fine spherical aluminum powder 40kg, oleic acid 4kg, ball milled at a speed of 50-200 rpm for 48h, discharge, filter press, and return the filtrate to the ball milling process for recycling.

[0014] (2) The filter cake enters the sieving and grading process. It passes through a 120-mesh sieve and then a 500-mesh sieve. The sieved materials at all levels are filtered and blow-dried with a filter press, and then fresh D 50 Organic solvent washing; the filtrate returns to the screening process for recycling.

[0015] (3) The filter cake enters the kneading process for surface treatment, and the packaging becomes a strong flashing aluminum silver paste product.

Example Embodiment

[0016] Example 2:

[0017] (1) In the φ800×1000 vertical stirring ball mill, 500kg of glass balls with a diameter of 1.0-5.0mm are loaded, and 200kg of D80 solvent oil is added, D 50 7.8μm nitrogen atomized fine spherical aluminum powder 80kg, oleic acid 4kg, ball milled at a speed of 50-200 rpm for 38 hours, discharge, filter press, and return the filtrate to the ball milling process for recycling;

[0018] (2) The filter cake enters the sieving and grading process, and passes through a 120-mesh sieve and then a 500-mesh sieve. The materials at all levels are filtered with a filter press, dried, and washed with fresh organic solvent; the filtrate returns to the sieve Recycled in different processes;

[0019] (3) The filter cake enters the kneading process for surface treatment, and the packaging becomes a strong flashing aluminum silver paste product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a manufacturing method of strong twinkling aluminium pastes. The manufacturing method comprises the following steps: in a vertical stirring mill, adopting glass beads with the diameter being 1.0-5.0mm to serve as milling medium of a ball mill; mixing uniformly the ultrafine spherical aluminium powder with d50 being greater than 8mu m and less than 10mu m, organic solvent and dispersing agent according to the ratio of 20-50:80-200:1-5; ball milling for 20-50h under the rotating speed being 50-200rpm, discharging, filter pressing, introducing the filter liquor to the ball milling procedure for recycling; classifying through fine screening; filter pressing the screened material at each stage by the filter press; blowing dry and reusing; filter pressing and washing through; carrying out surface treatment on the filter cakes entering the mediating procedure; controlling the thickness of the aluminium particles to be 1-2mu m; and packaging to obtain the finished products.

Description

technical field [0001] The invention relates to a method for preparing aluminum pigments in fine chemical industry, in particular to a method for manufacturing strong flashing aluminum-silver paste. Background technique [0002] The existing manufacturing methods of aluminum pigments mainly include dry production and wet production; the existing wet production includes (1) mixing aluminum powder with organic solvents, lubricants, etc. in a certain proportion and then grinding in a ball mill; (2) After sieving, press filter to make a filter cake, (3) surface treatment by kneading to become aluminum silver paste; but the existing wet production is to use large steel balls with a size of 1.5 mm or more, and ball mill for 15-25 hours to break the coarse aluminum powder into flakes , after sieving and passing through 500 mesh materials, press filter directly, the filtrate returns to the ball milling process, the filter cake is kneaded and surface treated, and the package is an al...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09C1/64C09C3/04C09D17/00
Inventor 夏风曾孟金苏力农姜小平刘顺治
Owner 长沙族兴新材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap