Deplating method for carbon-based thin film on surface of metal workpiece
A technology for metal workpieces and workpiece surfaces, which is applied in the field of removing surface vapor deposition coatings to achieve the effect of avoiding corrosion damage and smoothing the surface
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0027] Example 1: Decoating treatment after hot wire preparation of diamond coating on the surface of M2 steel test piece
[0028] An M2 steel test piece with a diamond coating of about 2 microns thick on the surface. The sample is black with a size of 100mmx30mmx2mm. The diamond coating is known to be prepared by the hot wire method, and the coating needs to be completely removed to obtain a smooth surface.
[0029] A method for stripping a carbon-based film on the surface of a metal workpiece includes the following steps:
[0030] 1) Put the M2 steel test piece with surface coating in an aqueous solution containing 5wt% of commercially available "Qiqiang" metal degreasing detergent, boil for about 5 minutes, rinse the test piece with clean city water and bake it Dry; Mount the M2 steel test piece with surface coating on the fixture and put it into the vacuum system.
[0031] 2) Close the door of the vacuum chamber and turn on the workpiece holder to rotate; the vacuum chamber is pum...
Example Embodiment
[0034] Example 2: Decoating treatment after preparing diamond-like carbon coating on the surface of 316L watch case
[0035] The 316L case with a diameter of 38mm is coated with a matrix / Cr / CrC / a-C:H diamond-like carbon coating, of which the surface diamond-like carbon coating is 1.2 microns, and the metal and its carbide transition layer is 1.2 microns. Due to the preparation of the coating, the coating is partially peeled off, the surface is black and gray, and occasionally there are white bright spots that can be seen by visual inspection, and it is necessary to remove the treated coating and recoat it.
[0036] A method for stripping a carbon-based film on the surface of a metal workpiece includes the following steps:
[0037] 1) Place the watch case in an aqueous solution containing 5wt% of commercially available "Qiqiang" metal degreasing detergent, boil for about 5 minutes, rinse the test piece with clean city water and dry it; hang the watch case on Put the vacuum system on ...
Example Embodiment
[0041] Example 3: Stripping treatment of Ti / TiN / AlTiN / graphite coating on the surface of H13 steel test piece
[0042] The surface of the H13 steel test piece with a size of 100mmx30mmx2mm is prepared with Cr / CrN / AlTiN / graphite coating. The thickness of the black graphite coating on the surface is 0.8 microns, and the thickness of the transition coating is 2 microns; the edges are wiped with 1500# water sandpaper. Drop to expose the substrate.
[0043] A method for stripping a carbon-based film on the surface of a metal workpiece includes the following steps:
[0044] 1) Put the test piece in an aqueous solution containing 5wt% of commercially available "Qiqiang" metal degreasing cleaner, boil for about 5 minutes, rinse the test piece with clean city water and dry it; hang the test piece on Put the vacuum system on the special fixture;
[0045] 2) Close the door of the vacuum chamber and turn on the workpiece holder to rotate; the vacuum chamber is pumped to the background and the va...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap