Manufacturing method of water tank of water heater

A technology for water heater tanks and manufacturing methods, applied to fluid heaters, lighting and heating equipment, etc., can solve the problems of poor corrosion resistance, high temperature resistance, high cost, etc., to improve heat resistance and corrosion resistance, and improve adhesion , Improve the effect of temperature resistance

Inactive Publication Date: 2010-06-16
曾赞伦 +2
View PDF0 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In the current existing technology, the water heater tank is made of copper material, and the cost is high
Made of alum

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 2

[0040] Silicone resin, aluminum silver paste, pigments and fillers and nano-scale ceramic beads are:

[0041] Silicone resin 60%, 2000 mesh aluminum silver paste 8%, pigment and filler 12%

[0042] Nanoscale ceramic microbeads 20%.

[0043] Wherein the coating made of silane, xylene and additives occupies a percentage of 10g / Kg of the silicone coating.

[0044] The ratio of silane, xylene and additives is:

[0045] Silane 60%, Xylene 20%, Auxiliary 20%

Embodiment 3

[0047] Silicone resin, aluminum silver paste, pigments and fillers and nano-scale ceramic beads are:

[0048] Silicone resin 80%, 2000 mesh aluminum silver paste 8%, pigments and fillers 8%, nano-scale ceramic microbeads 4%.

[0049] Wherein the coating made of silane, xylene and additives occupies a percentage of 30g / Kg of the silicone coating.

[0050] Prove by experiment: wherein silane, dimethylbenzene and auxiliary agent are made coating and the percentage that accounts for organic silicon coating is 50g / Kg, 70g / Kg or 80g / Kg all can reach the object of the present invention.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a manufacturing method of the water tank of a water heater, which is characterized by comprising the following steps: (1) manufacturing water tank parison; (2) carrying out alkali wash, oil removing, pickling and polishing; (3) coating an alloy layer; (4) coating a heat-resistant layer; and (5) self drying 30min at room temperature and then drying for 15min under the condition of 300-400 DEG C to obtain finished product. The temperature resistance of the surface of aluminum or aluminum material can be effectively improved by a zinc-nickel-titanium alloy layer, meanwhile, the adhesion of a subsequent coating is improved; and the heat resistance and the decay resistance of the heat-resistant layer are further improved. Compared with manufacturing by copper in the prior art, the cost is lowered; and compared with products manufactured by aluminum or aluminum alloy, the heat resistance and decay resistance are improved.

Description

technical field [0001] The invention relates to a manufacturing method of a water heater tank. Background technique [0002] In the current prior art, the water tank of the water heater is made of copper material, and the cost is high. If it is made of aluminum or aluminum alloy material, it is not resistant to high temperature, has poor corrosion resistance and is easy to damage. Contents of the invention [0003] The object of the present invention is to provide a method for manufacturing a water heater tank, which can make the water tank made of aluminum or aluminum alloy have high temperature resistance and corrosion resistance. [0004] The present invention is achieved like this: 1, a kind of manufacture method of water heater water tank, it is characterized in that: follow the steps: [0005] (1) Production of water tank parison [0006] The parison is made of ordinary metal aluminum or aluminum alloy material; [0007] (2) Alkaline washing to remove oil, pickli...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): F24H9/00
Inventor 曾赞伦李永斌蔡锡超
Owner 曾赞伦
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap