High-strength stretch-proof flame-retardant textile

A flame-retardant fabric, stretch-resistant technology, applied in the direction of fabrics, textiles, textiles and papermaking, can solve the problems of insufficient softness, easy to break, etc., and achieve the effect of soft hand feeling, no decrease in flame retardant performance, and good strength.

Inactive Publication Date: 2013-04-03
汕头市奥山服饰有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The inorganic fibers that play the role of cut resistance are metal fibers, so this fabric is very hard, not soft enough, and easy to break, not ideal for clothing or mattresses, seat fabrics

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The high-strength stretch-resistant flame-retardant fabric described in this embodiment is a flame-retardant fabric for welding protective clothing.

[0022] A flame-retardant fabric for welding protective clothing, which is woven from a flame-retardant composite yarn, and the flame-retardant composite yarn is composed of a core yarn and a sheath yarn; the flame-retardant composite yarn is a core-spun yarn; the The leather yarn in the core-spun yarn is the outsourcing fiber; the core yarn is made of flame-retardant filament raw material, and the leather yarn is made of ordinary flame-retardant staple fiber raw material; the flame-retardant filament is para-aramid fiber, and the The common flame-retardant staple fiber described above is melamine fiber; the weight ratio of the para-aramid fiber to the melamine fiber can be selected within the range of 30~90:10~70, and the preferred weight ratio is 40: 60; the fineness of the flame-retardant composite yarn is 22tex; the sq...

Embodiment 2

[0030] The high-strength stretch-resistant flame-retardant fabric described in this embodiment is a flame-retardant protective clothing fabric.

[0031] A fabric for flame-retardant protective clothing, which is woven from flame-retardant composite yarn, and the flame-retardant composite yarn is composed of core yarn and sheath yarn; the flame-retardant composite yarn is wrapping yarn, and the wrapping The cover yarn in the wrapping yarn is an outsourcing yarn; the core yarn is made of flame-retardant filament raw material, and the cover yarn is made of ordinary flame-retardant short fiber raw material; the flame-retardant filament is meta-aramid fiber, and the The common flame-retardant staple fiber described above is acrylic fiber; the weight ratio of the meta-aramid fiber to the acrylic fiber can be selected within the range of 30~90:10~70, and the preferred weight ratio is 70:30; the fineness of the flame-retardant composite yarn is 15tex; the square meter mass of the flam...

Embodiment 3

[0038] The high-strength stretch-resistant flame-retardant fabric described in this embodiment is a train seat flame-retardant fabric.

[0039] A flame-retardant fabric for a train seat, which is woven from a flame-retardant composite yarn, and the flame-retardant composite yarn is composed of a core yarn and a leather yarn; the flame-retardant composite yarn is a core-spun yarn, and the The leather yarn in the core-spun yarn is the outsourcing fiber; the core yarn is made of flame-retardant filament raw material, and the leather yarn is made of ordinary flame-retardant staple fiber raw material; the flame-retardant filament is polysulfone-based amide fiber, and the The common flame-retardant short fiber described above is flame-retardant polyester fiber; the weight ratio of the polysulfone-based amide fiber to the flame-resistant polyester fiber can be selected within the range of 30-90:10-70, and the preferred weight ratio 50:50; the fineness of the flame-retardant composite...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
smoldering timeaaaaaaaaaa
lengthaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention provides a high-strength stretch-proof flame-retardant textile. The flame-retardant textile is formed by weaving a flame-retardant composite yarn, wherein the flame-retardant composite yarn is formed by compounding a core yarn and a leather yarn and is one of a covering yarn and a fasciated yarn; the core yarn adopts a flame-retardant filament yarn as a raw material; the leather yarn adopts a flame-retardant short fiber as a raw material; and the weight ratio of the flame-retardant filament yarn to the flame-retardant short fiber is 30-90:10-70. Compared with the conventional flame-retardant textile, the high-strength stretch-proof flame-retardant textile has higher strength and overcomes the defects of difficult weaving, difficult dyeing and uncomfortableness of the high-strength fiber; the high-strength stretch-proof flame-retardant textile has permanent flame retardance which cannot decrease after the textile is washed, and better textile strength; the textile has soft and comfortable handfeel, rich color and good strength, meets the requirements of various flame-retardant clothes and related standards; the product has rich and varied appearances and is durable; and the combustion performance of the textile can meet the national standards of flame-retardant products.

Description

technical field [0001] The invention relates to a high-strength stretch-resistant flame-retardant fabric. The flame-retardant fabric is woven from a flame-retardant composite yarn; the flame-retardant composite yarn is composed of a core yarn and a leather yarn; the flame-retardant The composite yarn is one of core-spun yarn and wrapped yarn; the core yarn is made of flame-retardant filament raw material, and the cover yarn is made of flame-retardant staple fiber raw material. Background technique [0002] With the development of my country's economy, fire reports in various places are frequent, people's awareness of fire prevention is gradually increasing, relevant national laws, regulations and standards have been promulgated, and the requirements and demand for fire-resistant and flame-retardant fabrics are also increasing year by year. At present, with the continuous advancement of science and technology, the gradual improvement of industrial production and manufacturing...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D03D15/12D02G3/36D02G3/04D03D15/225D03D15/242D03D15/283D03D15/40D03D15/47D03D15/513D03D15/573
Inventor 吴汉荣
Owner 汕头市奥山服饰有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com