Polyvinyl alcohol film and method for producing the same
A polyvinyl alcohol film and polyvinyl alcohol-based technology, applied in the field of polyvinyl alcohol film and its manufacture, can solve the problems of reducing film retardation spots and inability to make films, so as to reduce striped dyeing spots and reduce wrinkles , Excellent optical properties
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0110] use figure 2 The barrel film making machine, makes the volatile component rate that is formed by the PVA of 100 mass parts saponification degree 99.9 mol%, average degree of polymerization 2400, 12 mass parts glycerol, 0.1 mass part lauric acid diethanolamide and water be 66 The film-forming stock solution 2 of mass % is discharged from the T die head 1 to the first drying roller 3 (the surface temperature is 94° C., and the peripheral speed is 14 m / min), and then peeled off with the second drying roller 4 a, and dried in the second drying roller. After rolling, drying is carried out at an average of 85°C. At this time, the drying roll having a volatile component rate of 16% by mass was the fifth drying roll, and the drying roll having a volatile component rate of 8% by mass was the tenth drying roll. Peripheral speed ratio S' / S of the drying rolls passing through this section (peripheral speed of the fifth drying roll: S, peripheral speed of the tenth drying roll: S'...
Embodiment 2
[0112] use figure 2 The barrel film making machine, makes the volatile component rate that is formed by the PVA of 100 mass parts saponification degree 99.9 mol%, average degree of polymerization 2400, 12 mass parts glycerol, 0.1 mass part lauric acid diethanolamide and water be 66 The film-forming stock solution 2 of mass % is spouted from the T die head 1 to the first drying roller 3 (the surface temperature is 93° C., and the peripheral speed is 14 m / min), and then peeled off with the second drying roller 4 a, and dried in the second drying roller. After rolling, drying is carried out at an average of 80°C. At this time, the drying roll having a volatile component rate of 16% by mass was the sixth drying roll, and the drying roll having a volatile component rate of 8% by mass was the eleventh drying roll. The peripheral speed ratio S' / S of the drying rolls passing through this section (peripheral speed of the sixth drying roll: S, peripheral speed of the 11th drying roll:...
Embodiment 3
[0114] use figure 2 The barrel film making machine, makes the volatile component rate that is formed by the PVA of 100 mass parts saponification degree 99.9 mol%, average degree of polymerization 2400, 12 mass parts glycerol, 0.1 mass part lauric acid diethanolamide and water be 66 The film-forming stock solution 2 of mass % is spouted from the T die head 1 to the first drying roller 3 (the surface temperature is 93° C., and the peripheral speed is 14 m / min), and then peeled off with the second drying roller 4 a, and dried in the second drying roller. After rolling, drying is carried out at an average of 80°C. At this time, the drying roll having a volatile component rate of 16% by mass was the sixth drying roll, and the drying roll having a volatile component rate of 8% by mass was the eleventh drying roll. Peripheral speed ratio S' / S of the drying rolls passing through this section (circumferential speed of the sixth drying roll: S, peripheral speed of the 11th drying roll...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap