A kind of ppo/pbt composite material for industrial large parts and preparation method thereof

A composite material, large-scale technology, applied in the field of PPO/PBT composite material and its preparation, can solve problems such as structural incompatibility, and achieve the effect of improving comprehensive performance, wide application and good economic benefits

Inactive Publication Date: 2011-12-07
SHENZHEN KEJU NEW MATERIAL
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the two materials, PPO and PBT, are completely incompatible in structure. In order to achieve the alloy effect and obtain broad application prospects, the compatibility of the two must be improved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] Weigh 20 parts of polybutylene terephthalate, 40.1 parts of polyphenylene ether, 24, 2 and 6 parts of toughening agents HIPS, SEBS and SBS, 6 parts of SMA grafts, and 6 parts of antioxidant 0.2 part of agent 1010 and 168, 0.5 part of lubricant TAF, and 1 part of flame retardant BDP to prepare PPO / PBT composite material.

[0045] Composite materials were prepared by the following methods:

[0046] a: First dry the polybutylene terephthalate resin and polyphenylene ether powder at 110°C and 120°C for 6 hours;

[0047] b: Use a high-speed mixer to mix the lubricant, compatibilizer and antioxidant at high speed, and then put it in a drying oven for drying. The drying temperature is 90°C and the drying time is 2 hours;

[0048] c: Put the raw materials processed in steps a and b into a high-speed mixer, then add toughening agent and oil flame retardant and mix evenly for 7 minutes;

[0049] d: Put the mixed raw materials in step c into the hopper of the twin-screw extruder...

Embodiment 2

[0051] Weigh 14.1 parts of polybutylene terephthalate, 55 parts of polyphenylene ether, 23, 2 and 4 parts of toughening agents HIPS, SEBS and SBS, 2 parts of SMA grafts, and 2 parts of antioxidant 10100.2 parts of lubricant, 0.5 parts of lubricant TAF, and 1 part of flame retardant BDP to prepare PPO / PBT composite materials.

[0052] Composite materials were prepared by the following methods:

[0053] a: First dry the polybutylene terephthalate resin and polyphenylene ether powder at 130°C and 130°C for 4 hours;

[0054] b: Use a high-speed mixer to mix the lubricant, compatibilizer and antioxidant at high speed, and then put it in a drying oven for drying. The drying temperature is 100°C and the drying time is 1 hour;

[0055] c: Put the raw materials processed in steps a and b into a high-speed mixer, then add toughening agent and oil flame retardant and mix evenly for 10 minutes;

[0056] d: Put the mixed raw materials in step c into the hopper of the twin-screw extruder,...

Embodiment 3

[0058] Weigh 12 parts of polybutylene terephthalate, 54.1 parts of polyphenylene ether, 23, 2 and 4 parts of toughening agent HIPS, SEBS and SBS respectively, 4 parts of SEBS graft, and 4 parts of antioxidant A total of 0.3 parts of agents 1010 and 168, 0.5 parts of lubricant TAF, and 1 part of flame retardant BDP were used to prepare PPO / PBT composite materials.

[0059] Composite materials were prepared by the following methods:

[0060] a: First dry the polybutylene terephthalate resin and polyphenylene ether powder at 120°C and 125°C for 6 hours;

[0061] b: Use a high-speed mixer to mix the lubricant, compatibilizer and antioxidant at high speed, then put it in a drying oven for drying, the drying temperature is 95 ° C, and the drying time is 2 hours;

[0062] c: Put the raw materials processed in steps a and b into a high-speed mixer, then add toughening agent and oil flame retardant and mix evenly for 6 minutes;

[0063] d: Put the mixed raw materials in step c into t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a PPO / PBT composite material used for industrial large-scale parts and a preparation method thereof. The composite material comprises the following components in terms of weight percentage: 30% to 55% of polyphenylene ether (PPO), polyparaphenylene Butylene glycol diformate (PBT) 8-25%, toughening agent 13.6-32%, compatibilizer 6-15%, antioxidant 0.2-0.8%, lubricant 0.2-0.6%, flame retardant 1-6 %. The invention improves the incompatibility between PPO and PBT materials due to the structure by adopting a suitable compatibilizer, and solves the defect of peeling of PPO / PBT composite materials in the injection molding process, and poor fluidity, which is difficult to form The defects of large parts greatly improve the comprehensive performance of PPO / PBT composite materials, making forming parts easier and more widely used, and the preparation process is simple and low cost, which can achieve good economic benefits.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to a PPO / PBT composite material used for large-scale industrial parts and a preparation method thereof. Background technique [0002] Polyphenylene oxide (PPO) is one of the world's five general-purpose engineering plastics. It has the advantages of high rigidity, high heat resistance, flame retardant, high strength and excellent electrical properties. In addition, polybenzyl ether also has the advantages of wear resistance, non-toxicity, and pollution resistance. The dielectric constant and dielectric loss of PPO are one of the smallest varieties among engineering plastics, and they are hardly affected by temperature and humidity, and can be used in low, medium and high frequency fields. The load deflection temperature of PPO can reach above 190°C, and the embrittlement temperature is -170°C. Unmodified polyphenylene ether (PPO) resin has good mechanical properties, el...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L71/12C08L67/02C08L51/06C08L51/08B29B9/06B29C47/92B29C48/40B29C48/92
CPCB29C48/92B29C2948/92704B29C48/04B29C48/40B29C48/9185B29C2948/92514B29C2948/92561B29C2948/92895B29C2948/92904
Inventor 郭宇嘉
Owner SHENZHEN KEJU NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap