Bonding agent of baking-free bricks prepared from drilling well solid waste materials

A technology of solid waste and cement, which is applied in the field of oil drilling and can solve problems such as high cost, deformation, and easy cracks in unburned bricks

Active Publication Date: 2010-08-18
PETROCHINA CO LTD
View PDF3 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to provide a kind of unburned brick cement made from drilling solid waste, and to make a kind of unburned brick cement made from drilling solid waste to overcome the easy crack, deformation and strength of unburned brick made from drilling solid waste. low cost problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Embodiment 1: drilling solid waste system unburned brick cement, each component weight part is: polyaluminum chloride 4 parts; Phosphogypsum 7 parts; Quicklime 24 parts; Fly ash 60 parts; Ferrous sulfate 5 parts, The components are mixed and stirred uniformly to obtain the non-burning brick cement made from drilling solid waste.

[0017] The method for preparing non-burning bricks by using the unburned brick cement made from drilling solid waste is: the parts by weight of each component of the unburned brick are: 15 parts of unburned brick cement made from drilling solid waste; Longgang 9 wells, Guang'an 10 wells 37 parts of drilling solid waste from the five wells of Well Guang'an 143, Well Guang'an 002-H2-X3 and Well Moxi 005-H12; 48 parts of coarse aggregate, mixed evenly, extruded by an unfired brick making machine, and maintained for 19 hours Days, made of unburned bricks. Coarse aggregates are waste brick chips with a particle size of 4.75-5.75 mm.

[0018] The ...

Embodiment 2

[0019] Example 2: An unburned brick cement made from drilling solid waste, the weight ratio of each component is: 5 parts of polyaluminum chloride; 10 parts of phosphogypsum; 21 parts of quicklime; 50 parts of fly ash; 7 parts of ferrous sulfate. Mix the ingredients together and stir well.

[0020] The method for preparing non-burning bricks by using the unburned brick cement made from drilling solid waste is as follows: the weight ratio of each component of the unburned brick is: 20 parts of unburned brick cement made from drilling solid waste; 40 parts of drilling solid waste; 40 parts of coarse aggregate, mixed evenly, extruded by an unfired brick machine, cured for 20 days, and made into 6,000 pieces of unfired bricks for the reconstruction of earthquake-stricken houses in Qionglai County, Sichuan. Coarse aggregate is coal gangue with a particle size of 5.75-6.75 mm.

Embodiment 3

[0021] Example 3: Unburned brick cement made from drilling solid waste, the weight ratio of each component is: 3.6 parts of polyaluminum chloride; 13 parts of phosphogypsum; 19 parts of quicklime; 44 parts of fly ash; 5 parts of ferrous sulfate. Mix the ingredients together and stir well.

[0022] The method for preparing non-burning bricks by using drilling solid waste to prepare non-burning brick cement is as follows: the weight ratio of each component of making non-burning bricks is: 17 parts of non-burning brick cement made from drilling solid waste; 43 parts of drilling solid waste; 40 parts of coarse aggregate, mixed evenly, extruded by an unfired brick machine, cured for 20 days, and made into an unfired brick. Coarse aggregate is coal gangue with a particle size of 6.75-7.75 mm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to a bonding agent of baking-free bricks prepared from drilling well solid waste materials, which is applied to the field of treating petroleum drilling well solid waste materials into resources for preparing baking-free bricks. The bonding agent comprises the following ingredients in parts by weight: 3.3 to 8 of polyaluminium chloride, 6 to 25 of phosphogypsum, 10 to 26 of lime, 20 to 60 of fly ash and 4.4 to 12 of ferrous sulfate. A method for using drilling well solid waste materials for preparing the baking-free bricks comprises the following steps that: the baking-free bricks are prepared from the following ingredients in parts by weights: 10 to 22 of bonding agents of baking-free bricks prepared from drilling well solid waste materials, 30 to 55 of drilling well solid waste materials and 35 to 45 of crude aggregate; and the ingredients are uniformly mixed, are extruded and formed through a baking-free brick machine, and are maintained for 14 to 21 days to prepare the baking-free bricks. The invention has the advantages that the baking-free bricks can be prepared, and through the analysis via the sampling and the water soaking experiments on the baking-free bricks, all contaminant indexes reach the primary standard. Through the examination according to the standard JC422-1991, the detected items of the samples reach the requirements of the standard.

Description

technical field [0001] The invention relates to the technical field of petroleum drilling, in particular to resource treatment of drilling solid waste, and is a cement for making unburned bricks from drilling solid waste. Background technique [0002] At present, drilling solid waste mainly includes drilling waste mud and drilling cuttings. Drilling waste mud is a stable gel system with high water content, mainly composed of bentonite, barite and mud treatment agent, etc., and also mixed with a small amount of cuttings and drilling additives. Generally, the water content is about 90%, and bentonite accounts for about 5%. %. Drilling cuttings are mainly formation cuttings produced during the drilling process. [0003] Drilling solid waste unburned bricks is a technology researched on the comprehensive utilization technology of drilling solid waste. Due to the characteristics of low soil content and high barite powder content in drilling mud, appropriate amount of coarse ag...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/14C04B18/12
CPCY02W30/91
Inventor 陆林峰向启贵银小兵易畅范有余
Owner PETROCHINA CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap