Polymer vitrified microsphere building heat-insulating mortar

A technology of building thermal insulation mortar and vitrified microbeads, which is applied in the field of building materials, can solve problems such as insufficient strength, poor bonding and wrapping properties, and poor waterproof performance, so as to reduce material costs, improve cohesiveness, and enhance crack resistance sexual effect

Inactive Publication Date: 2010-08-25
河南省绿韵建材有限公司
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing materials have defects and deficiencies such as poor bonding and wrapping properties, poor waterproof performance, insufficient strength, easy slag drop, troublesome construction and high cost.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0019] In the specific implementation, as long as a set of mortar mixing equipment is purchased, qualified products can be organized. The production sequence is as follows: the first step is to prepare a special admixture; the second step is to prepare a mixed cementitious powder; the third step is to mix the thermal insulation mortar of the present invention. The thermal insulation mortar product of the present invention can be used in a single-component delivery site by adding water and stirring as required. Specifically, in this embodiment, the thermal insulation mortar mixture is prepared according to the following method:

[0020] ① The mixed raw materials of the thermal insulation mortar mixture produced in this embodiment are mixed cementitious powder and vitrified microbeads. According to the volume ratio, mix the cementitious powder: vitrified beads = (V) 1: (V) 4.5. The corresponding mass ratio is: mixed cementing powder: vitrified beads = 1:0.6. The loose bulk densi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
compressive strengthaaaaaaaaaa
shrinkageaaaaaaaaaa
Login to view more

Abstract

The invention discloses a polymer vitrified microsphere building heat-insulating mortar. The preparation of the heat insulating mortar is implemented by the following steps: firstly, preparing a special additive; secondly, preparing mixed cementitous powder; and finally, uniformly mixing the mixed cementitous powder and vitrified microspheres in a weight ratio of 1:0.6 to obtain the polymer vitrified microsphere building heat-insulating mortar. The heat-insulating mortar of the invention, on the premise of meeting national standards in performance, is improved in bonding strength and lowered in manufacturing cost and suitable for use in projects of interior and exterior plastering of mid- and high-rise building walls made of various materials, particularly, projects of old building heat-insulating modification.

Description

Technical field [0001] The invention relates to the technical field of building materials, in particular to a building insulation mortar with polymer vitrified microspheres. Background technique [0002] Building thermal insulation mortar, as one of the thermal insulation materials of the building's outer protective structure, its principle is to add lightweight aggregate to the wall plastering mortar to reduce the density of the mortar and increase the heat resistance of the material. Its composition is mostly composed of cement binder, expanded perlite, foam particles and other light aggregates. However, the existing materials have the defects and deficiencies of poor bonding and binding properties, poor waterproof performance, insufficient strength, easy slag drop, troublesome construction, and high cost. Summary of the invention [0003] In view of this, the purpose of the present invention is to provide a polymer vitrified microbead building thermal insulation mortar, which ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B18/08
CPCC04B2111/28C04B28/14Y02W30/91C04B7/02C04B14/106C04B14/24C04B14/4643C04B18/08C04B18/24C04B20/008C04B22/064C04B24/226C04B24/26C04B24/383C04B40/0028C04B2103/65C04B2103/0057C04B2103/302
Inventor 郭长顺丁仲勋谷亚南
Owner 河南省绿韵建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap