Easy-cutting high strength zinc alloy

A high-strength, zinc alloy technology, applied in the field of new alloy materials, can solve the problems of high cost and achieve the effects of high dimensional stability, low thermal processing temperature and high tensile strength

Inactive Publication Date: 2010-10-06
绍兴市天龙锡材有限公司
View PDF5 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The essence of the invention is to add trace amounts of copper, aluminum, magnesium and rare earth lanthanum and cerium to the zinc alloy. Among them, the content of copper, magnesium and rare earth is relatively high, so the cost is relatively high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Easy-cutting high strength zinc alloy

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] The composition of each component of the zinc alloy is calculated by weight percentage, which are: aluminum 22%, copper 1%, magnesium 0.01%, bismuth 0.1%, manganese 0.1%, the total amount of impurities is not more than 0.05%, the balance is zinc, each The sum of the weight percentages of the components is 100%.

Embodiment 2

[0020] The composition of each component of the zinc alloy is calculated by weight percentage, which are: aluminum 15%, copper 1.25%, magnesium 0.03%, bismuth 0.005%, antimony 0.01%, manganese 0.07%, the total amount of impurities is not more than 0.05%, the balance For zinc, the weight percentage sum of each component is 100%.

Embodiment 3

[0022] The composition of each component of the zinc alloy is calculated by weight percentage, which are: aluminum 12%, copper 1.5%, magnesium 0.05%, antimony 0.04%, manganese 0.05%, the total amount of impurities is not more than 0.05%, the balance is zinc, each The sum of the weight percentages of the components is 100%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an easy-cutting high strength zinc alloy. Most of current Zn-Al series alloys have the defects of poor cutting performance, inter-granular corrosion tendency, low dimensional stability, low working temperature, poor creep resistance, poor corrosion resistance and the like. The zinc alloy is characterized by comprising the following components in percentage by weight: 1 to 25 percent of aluminum, 0.5 to 3.5 percent of copper, 0.005 to 0.3 percent of magnesium, 0.01 to 0.1 percent of manganese, 0.005 to 0.15 percent of bismuth or/and 0.01 to 0.1 percent of antimony, no more than 0.05 percent of impurities and the balance of zinc. The strength of the zinc alloy can be effectively improved; the zinc alloy has good cutting performance and certain plastic processing performance; the raw materials are cheap, easily obtained and environment-friendly; and the zinc alloy is an ideal material for replacing current domestic lead-containing brass and partial stainless steel parts.

Description

technical field [0001] The invention relates to the field of new alloy materials, in particular to a free-cutting high-strength zinc alloy, which is used to replace lead brass to make electronic and electrical connectors, instrument parts, plumbing and sanitary parts, and automobile and motorcycle spare parts. Background technique [0002] Since the 1920s, with the massive mining and consumption of copper resources, there has been a tense situation of copper resources all over the world. In the face of rising copper prices, our country, which is inherently deficient in copper resources, is imminent in finding copper alloy substitute materials. . Lead brass has excellent cutting performance and wear resistance, and is widely used in electronic and electrical connectors, instrument parts, plumbing and sanitary parts, and automobile and motorcycle parts. However, because lead is contained therein, lead is easy to dissolve, causing environmental pollution and endangering people...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C18/04
Inventor 戴国水钱国统
Owner 绍兴市天龙锡材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka