A technology of LED lamp tube and high haze, applied in the field of polymer materials, can solve the problems of weakened penetrating power and large loss, and achieve the effect of high transparency and simple preparation process

Inactive Publication Date: 2010-11-10
SHENZHEN KEJU NEW MATERIAL
View PDF4 Cites 32 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The traditional processing modification method is to add some inorganic additives, such as silicon dioxide and barium sulfate, to PC or PMMA. Adding these inorganic nanoparticles, the light will undergo countless light refraction

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Mix the diffuser 0.3% by weight and EBS dispersant 0.3% in a plastic container evenly, then mix 98.6% PC engineering plastics and white oil 0.2% color protection agent 0.2% in another plastic container, and then mix well The astigmatizing agent and engineering plastics and 0.4% blue powder are put into a high-speed mixing container, and mixed at high and low speed for 3-5min at room temperature. Afterwards, the mixed materials are put into the hopper of the twin-screw extruder, melted and blended, extruded and granulated to form a composite material. Among them, the processing temperature settings of each zone of the screw are: the temperature of the first zone is 160-180°C, the temperature of the second zone is 240-260°C, the temperature of the third zone is 270-280°C, the temperature of the fourth zone is 270-280°C, the temperature of the fifth zone is 270-280°C, The temperature of the sixth zone is 270-280°C, the temperature of the seventh zone is 270-280°C, the temp...

Embodiment 2

[0030] Mix the diffuser 0.5% by weight and EBS dispersant 0.3% in a plastic container, then mix 98.4% PC engineering plastics and white oil 0.2% color protection agent 0.2% in another plastic container, and then mix well The astigmatizing agent and engineering plastics and 0.4% blue powder are put into a high-speed mixing container, and mixed at high and low speed for 3-5min at room temperature. Afterwards, the mixed materials are put into the hopper of the twin-screw extruder, melted and blended, extruded and granulated to form a composite material. Among them, the processing temperature settings of each zone of the screw are: the temperature of the first zone is 160-180°C, the temperature of the second zone is 240-260°C, the temperature of the third zone is 270-280°C, the temperature of the fourth zone is 270-280°C, the temperature of the fifth zone is 270-280°C, The temperature of the sixth zone is 270-280°C, the temperature of the seventh zone is 270-280°C, the temperature...

Embodiment 3

[0032] Mix the diffuser 0.8% by weight and EBS dispersant 0.3% in a plastic container, then mix 98.1% PC engineering plastics and white oil 0.2% color protection agent 0.2% in another plastic container, and then mix well The astigmatizing agent and engineering plastics and 0.4% blue powder are put into a high-speed mixing container, and mixed at high and low speed for 3-5min at room temperature. Afterwards, the mixed materials are put into the hopper of the twin-screw extruder, melted and blended, extruded and granulated to form a composite material. Among them, the processing temperature settings of each zone of the screw are: the temperature of the first zone is 160-180°C, the temperature of the second zone is 240-260°C, the temperature of the third zone is 270-280°C, the temperature of the fourth zone is 270-280°C, the temperature of the fifth zone is 270-280°C, The temperature of the sixth zone is 270-280°C, the temperature of the seventh zone is 270-280°C, the temperature...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-fog-degree and high-transparency LED lamp tube material and a preparation method thereof. The LED lamp tube material comprises the following components by weight ratio (%): 97-99% of engineering plastic, 0.3-1% of light-scattering agent; 0.3-1% of dispersant; 0.2-0.6% of color protection agent and 0.1-3% of other additives. The invention uses the engineering plastic PC as a main body, and adds the organic bead resin light-scattering agent, the color protection agent and other additives to carry out extrusion granulation by melt blending. The polycarbonate engineering plastic prepared by the invention can be used for extrusion molding of the LED lamp tube material, not only has good scattering effect but also has high luminousness, and has excellent physical and mechanical performances and simple process. The preparation method of the LED lamp tube material comprises the following process steps: firstly, mixing raw materials in proportion; then sending into a plastic extrusion machine, and controlling the temperature between 250 DEG C and 300 DEG C; and finally, carrying out granulation.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to a high haze and high transparency LED lamp tube material and a preparation method thereof. Background technique [0002] At present, due to the requirements of environmental protection and energy saving, the demand for LED lights has developed into a trend, but the LED light is strong and dazzling, and the light energy is high. How to make the light of the LED soft and minimize the loss of light energy has become an urgent technical problem to be solved in the application of LED lights today. [0003] To solve this problem, LED lamp shades can be added. PC and PMMA can be used as lampshade materials, but due to the high light transmittance of PC and PMMA, if they are not processed and modified, the light of LED lights will still be strong and dazzling. [0004] The traditional processing modification method is to add some inorganic additives, such as silicon dioxide a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L69/00C08L33/12C08K5/103C08K5/20B29C47/92B29C48/92
CPCB29C48/04B29C48/875B29C48/92B29C2948/92514B29C2948/92561B29C2948/92704B29C2948/92895
Inventor 徐东徐永刘洁
Owner SHENZHEN KEJU NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap