Application of carbazole oxime ester compound serving as photoinitiator in photopolymerisable acrylate composition

An acrylate and acrylate technology, used in optics, optical filters, optomechanical equipment, etc., can solve the problem of poor specific selectivity of photopolymerizable monomers, high transparency and photolithography residues, and insufficient short-wavelength sensitivity. problem, to achieve excellent curing effect, high short-wavelength sensitivity, and no scum

Active Publication Date: 2010-11-24
CHANGZHOU TRONLY NEW ELECTRONICS MATERIALS
View PDF4 Cites 40 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, these photoinitiators have more or less low sensitivity (high polymerization rate and exposure dose), poor solubility (more transparency and photolithographic residue), low storage stability, insufficient short-wavelength sensitivity, Defects such as poor selectivity to specific photopolymerizable monomers, which affect the performance of photosensitive materials as a whole

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Application of carbazole oxime ester compound serving as photoinitiator in photopolymerisable acrylate composition
  • Application of carbazole oxime ester compound serving as photoinitiator in photopolymerisable acrylate composition
  • Application of carbazole oxime ester compound serving as photoinitiator in photopolymerisable acrylate composition

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-1

[0038] (1) Colored curable (photopolymerizable) composition No. 1-1

[0039] Colorant (carbon black) 300 parts by mass

[0040] 200 parts by mass of alkali-soluble resin

[0041] (Benzyl methacrylate / methacrylic acid / hydroxyethyl methacrylate (molar ratio 70 / 10 / 20) total

[0042] Polymer (Mw: 10,000))

[0043] 100 parts by mass of dipentaerythritol hexaacrylate

[0044] Formula (I) oxime ester compound [n=2, m=3] 60 parts by mass

[0045] Surfactant FC-4430 1 part by mass

[0046] (2) Preparation of filter color film

[0047] The components of the above composition were mixed and dissolved in 1000 parts by mass of a solvent, propylene glycol methyl ether acetate (PGMEA), to form a liquid composition.

[0048] Use a spin coater to coat the liquid composition on a glass substrate, dry it at 90°C for 2 minutes, and form a coating film with a film thickness of 1.5 μm; in order to obtain a coating film with the above thickness, the coating process can be completed once or Do...

Embodiment 1-2

[0075] Use the formula (I) oxime ester compound of n=2, m=4 to replace the oxime ester compound in embodiment 1-1, other unchanged, prepare in the same way, and with the same method of embodiment 1-1 method to evaluate. The results are shown in Table 1.

Embodiment 2-1

[0083] (1) Colored curable composition No.2-1

[0084] Colorant C.I. Pigment Red 254 60 parts by mass

[0085] 80 parts by mass of alkali-soluble resin

[0086] [Benzyl methacrylate / methacrylic acid / hydroxyethyl methacrylate / acrylic ester of formula (II) (55 / 10 / 15 / 10 in molar ratio) copolymer] (Mw: 12,000)

[0087] 35 parts by mass of dipentaerythritol hexaacrylate

[0088] Formula (I) oxime ester compound [n=2, m=3] 20 parts by mass

[0089] Surfactant FC-4430 0.1 parts by mass

[0090] (2) Preparation of filter color film

[0091] The components of the above composition were mixed and dissolved in 100 parts by mass of a solvent, propylene glycol methyl ether acetate (PGMEA), to form a liquid composition.

[0092] Use a spin coater to coat the liquid composition on a glass substrate, dry it at 90°C for 2 minutes, and form a coating film with a film thickness of 1.5 μm; in order to obtain a coating film with the above thickness, the coating process can be completed once o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an application of a carbazole oxime ester compound serving as a photoinitiator in a photopolymerisable acrylate composition, the photopolymerisable acrylate composition containing the carbazole oxime ester compound and an application thereof. The composition presents excellent suitability by the combination of the specific photoinitiator and specific photopolymerisable acrylate monomer, and has high storage stability, higher light sensitivity in a short wave position, and excellent dissolvability performance; and when the composition is polymerized, the composition has the advantages of fast solidification speed, little pollution, energy conservation, high exposal efficiency and small exposal dosage, meanwhile, the solidified image pattern is fine and complete without defect and scum, and the membrane has good hardness.

Description

technical field [0001] The present invention relates to the use of a carbazole oxime ester compound as a photoinitiator in a photopolymerizable acrylate composition, the above photopolymerizable acrylate composition containing the carbazole oxime ester compound, and its application . Background technique [0002] Photocuring refers to the curing process of monomer, oligomer or polymer matrix under light induction. This technology has a wide range of applications in modern microelectronics technology, such as photocurable ink, liquid crystal panel packaging, photosensitive printing plate, Filters and photoresists, etc. The core of photocuring technology lies in photocurable polymerized monomers and suitable photoinitiators. Under the irradiation of ultraviolet / visible light, X-ray or laser at a certain wavelength, the photoinitiator generates active groups, which excites the unsaturated groups in the polymerizable monomer to undergo polymerization reaction, thereby causing ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08F2/48C08F265/06G03F7/027G02B5/20
Inventor 钱晓春胡春青王兵
Owner CHANGZHOU TRONLY NEW ELECTRONICS MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More