Method for inhibiting corrosion of butyl rubber chloromethane glycol dehydration system

A technology of butyl rubber and methyl chloride is applied in the field of inhibiting the corrosion of methyl chloride glycol dehydration system of butyl rubber, and can solve the problems of affecting the dehydration performance of glycol, increasing the scale of the device, consuming methyl chloride, etc. Corrosion, anti-corrosion effect

Active Publication Date: 2010-11-24
CHINA PETROLEUM & CHEM CORP
View PDF2 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since alcohol amines can react with methyl chloride to generate quaternary ammonium salts, glycol solution containing 10% to 30% alcohol amines will greatly consume methyl chloride on the one hand, and high-concentr

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Ethanolamine was added to triethylene glycol to make its concentration 1000mg / L glycol (0.1% by weight), heated to 150° C., and passed into methyl chloride gas until the chloride ion concentration was constant, the pH value of the system was 6.9, and the chloride ion was 536mg / L, iron ion is 5.9mg / L, and the corrosion rate of carbon steel is 0.046mm / a.

Embodiment 2

[0036] Ethanolamine was added to triethylene glycol to make its concentration 6000mg / L glycol (0.6% by weight), heated to 150° C., and passed into methyl chloride gas until the chloride ion concentration was constant, the pH value of the system was 7.4, and the chloride ion was 3187mg / L, iron ion is 4.7mg / L, and the corrosion rate of carbon steel is 0.037mm / a.

Embodiment 3

[0038] Ethanolamine was added to triethylene glycol to make its concentration 10000mg / L glycol (1% by weight), heated to 150° C., and the chlorine methane gas was introduced until the chloride ion concentration was constant, the pH value of the system was 7.4, and the chloride ion was 5228mg / L, iron ion is 3.5mg / L, and the corrosion rate of carbon steel is 0.027mm / a.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Corrosion rateaaaaaaaaaa
Corrosion rateaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for inhibiting corrosion of a butyl rubber chloromethane glycol dehydration system. The method is characterized by comprising the following steps of: adding alkylol amine into a chloromethane glycol dehydration and regeneration system; and removing chloride ions and iron ions produced in the system by using an anion exchange resin, wherein both steps cannot be saved. By using the technical scheme, a small amount of the alkylol amine is added, so the corrosion speed of carbon steel can be controlled, so that a small amount of the chloromethane is consumed and the loss of chloromethane solvent is reduced; meanwhile, the concentration of the chloride ions in the system is low and the corrosion to the carbon steel is also low; and the chloride ions and the iron ions can be removed by adopting the anion exchange resin, so the concentrations of the chloride ions and the iron ions are further reduced. Because the amount of hydrochloric acid produced by hydrolyzing the chloromethane is reduced, and the hydroxyl ions produced after the anion exchange resin exchanges the chloride ions neutralize the hydrogen ions of the system, the corrosion of the glycol dehydration and regeneration system can be greatly reduced.

Description

technical field [0001] The invention relates to a method for inhibiting the corrosion of a methyl chloride glycol dehydration system of butyl rubber, in particular to a method that focuses on solving the problem that when a butyl rubber device uses glycol to remove trace water in methyl chloride, because methyl chloride contains Hydrolysis of hydrogen chloride and methyl chloride in glycol to produce hydrochloric acid and lead to system corrosion. Background technique [0002] Butyl rubber is a rubber obtained by copolymerization of monomer isobutylene and a small amount of isoprene dissolved in the solvent methyl chloride at low temperature. Ozone, weather resistance, electrical insulation and other characteristics. Butyl rubber is mainly used in automobile bias tire inner tubes, radial tires, wires and cables, sealing materials, etc. [0003] In the production process of butyl rubber, the unreacted solvent methyl chloride and the unconverted monomers isobutylene and isop...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08F210/12C08F6/00
Inventor 华炜梁爱民郦和生王亭王岽李博伟李长玥冯婕
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap