Method for improving mixing ratio of burning ash in cement raw materials

A technology for incinerating ash and cement raw materials, which is applied in cement production and other directions to achieve the effects of reducing the content of harmful components, good experimental reproducibility and low cost

Active Publication Date: 2012-12-05
ZHEJIANG GONGSHANG UNIVERSITY
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In the current research and reports, it is still rare to see a method aimed at increasing the blending ratio of incineration ash in raw meal under the premise of ensuring the stable operation of cement production and product quality

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for improving mixing ratio of burning ash in cement raw materials
  • Method for improving mixing ratio of burning ash in cement raw materials
  • Method for improving mixing ratio of burning ash in cement raw materials

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Step 1: Original Characterization Analysis

[0037] A certain household waste incineration fly ash is taken from a certain place in Zhejiang Province, hereinafter referred to as fly ash 1#.

[0038] A certain industrial hazardous waste incineration fly ash is taken from a place in Zhejiang Province, hereinafter referred to as fly ash 2#.

[0039] A cement plant actually selects the following cement raw materials: limestone is selected as the calcareous raw material, shale is selected as the clay-based raw material, copper slag is selected as the iron-based calibration raw material, and quartz sand is selected as the siliceous calibration raw material.

[0040] The main components of the above fly ash 1#, fly ash 2# and several cement raw materials are as follows:

[0041] Table 1 Main chemical components of incineration fly ash and cement raw materials

[0042]

[0043] Note 1 Alkali content according to Na 2 O+0.658K 2 O calculated value means;

[0044] It can be...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a test method capable of effectively improving the mixing ratio of burning ash in cement raw materials. The method comprises the following steps of: analyzing original characteristics; performing washing pretreatment; firing ingredients to form clinker; and testing index and toxicity of the cement. The test method is designed completely aiming at a practical project, the raw materials are all the actual raw materials of a cement factory and the mixing ratio is also the actual production control ratio of the cement factory; the test method is well instructive to the project application; and on the premise of realizing stable operation of cement production and guaranteeing production quality, the test method greatly improves the mixing ratio of the burning ash in the cement raw materials. The whole test has the advantages of relatively a few involved large instruments, convenient operation, low cost and high test reproducibility.

Description

technical field [0001] The invention relates to the field of solid waste disposal, in particular to a method for increasing the mixing ratio of incineration ash and slag in cement raw materials. Background technique [0002] In recent years, the emerging international solid waste co-processing technology in cement kilns provides a new development direction for the realization of incineration ash treatment and resource utilization because it avoids the secondary treatment and turnover pollution of incineration ash. [0003] However, because the chlorine, sulfur, alkali and other components contained in the incineration ash are the inducements that cause crusting and blockage in the cement kiln, it is easy to cause frequent shutdown accidents, which greatly limits its application in cement production, especially chloride ions, cement The industry has very strict limits (no more than 0.03%) for chloride ions in raw materials. In order to ensure that the content of harmful comp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B7/28C04B7/38
CPCY02P40/10
Inventor 沈东升郑元格冯华军邓友华冯小晏郭梦婷陈应强徐栋张弛廖燕宋二喜
Owner ZHEJIANG GONGSHANG UNIVERSITY