High-performance elastic composite abrasive sheet and preparation method thereof

A high-efficiency, abrasive sheet technology, used in grinding/polishing equipment, abrasives, grinding devices, etc., to prevent deformation, good adhesion, and high tensile strength

Active Publication Date: 2011-02-09
JIANGSU FENGMANG COMPOUND MATERIAL SCI&TECH GRP CO LTD
View PDF14 Cites 28 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Although the above mentioned specific solutions to the problems of steel paper sanding discs from different a

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-performance elastic composite abrasive sheet and preparation method thereof
  • High-performance elastic composite abrasive sheet and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Using 0.8mm steel paper (23±1℃, 50±2%RH): tensile strength: >90MPa (MD), >45MPa (CD); elongation: 1.25g / cm3; Bursting strength >2000kPa; Corundum, for electrostatic sand planting; the weight ratio formula of the primer and the compound glue is as follows:

[0034] Table 1 The weight ratio formula of bottom compound glue

[0035]

[0036] The preparation method of high-efficiency elastic composite abrasive sheet comprises a primer application process, a sand planting process, a compound glue process, a post-curing process, a kneading and watering process, a laser cutting process, and a storage process; Curling, kneading and watering process and then use the sand surface to curl inward.

[0037] The curing process of the primer after sand planting is as follows: 60°C / 10min+75°C / 20min+90°C / 20min; 20min+100℃ / 10min; then perform post-curing at 118℃ / 6 hours, after cooling, perform 90° one-way kneading, with water 9g / m 2 , after 24 hours of parking, laser cutting, packag...

Embodiment 2

[0039] Using 0.8mm steel paper (23±1℃, 50±2%RH): tensile strength: >90MPa (MD), >45MPa (CD); elongation: 1.25g / cm3; Bursting strength >2000kPa; Adopt 100# first-class high temperature Calcined alumina for electrostatic sand planting; the weight ratio formula of primer and compound glue is as follows:

[0040] Table 2 The weight ratio formula of bottom compound glue

[0041]

[0042]The preparation method of the high-efficiency elastic composite abrasive sheet comprises a bottoming process, a sand planting process, a compounding process, a post-curing process, a kneading and watering process, a laser cutting process, a steel paper anti-deformation treatment process, and a storage process; In the curing process, the sand surface is used to curl outward, and after the kneading and watering process, the sand surface is used to curl inward.

[0043] The curing process of the primer after sand planting is as follows: 60°C / 10min+75°C / 20min+90°C / 20min; 20min+100℃ / 10min; then perf...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Gel timeaaaaaaaaaa
Thicknessaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the field of coated abrasives, and relates to a high-performance elastic composite abrasive sheet and a preparation method thereof. The high-performance elastic composite grinding sheet comprises a vulcanized paper back base, bottom glue, abrasive and complex glue, wherein the bottom glue comprises the following compositions in percentage by weight: 25 to 40 percent of phenolic resin A, 15 to 40 percent of phenolic resin B, 30 to 58 percent of fillers, 0.1 to 1.5 percent of surfactant and 0.1 to 15 percent of diluent; and the complex glue comprises the following compositions in percentage by weight: 15 to 70 percent of phenolic resin C, 15 to 70 percent of phenolic resin D, 0.1 to 3 percent of efficient flatting agent, 5 to 60 percent of fillers, 0.1 to 1.0 percent of coupling agent, 1 to 5 percent of pigment, and 0.1 to 10 of thinner. The method for preparing the high-performance elastic composite abrasive sheet comprises the steps of bottom glue coating process, grain coating process, complex glue coating process, post curing process, curly sand surface flatting process, laser cutting process, vulcanized paper deformation preventing process and storage process, wherein in the post curing process, the sand surface is curly outwards, and after the curly sand surface flatting process, the sand surface is curly inwards so as to enable the sand surface to be flat. The invention can effectively prevent deformation, and has the advantages of strong tensile strength, good adhesive performance and strong grinding performance.

Description

technical field [0001] The invention belongs to the field of coated abrasives, and relates to a high-efficiency elastic composite abrasive sheet and a preparation method thereof. Background technique [0002] Steel paper sanding disc, also known as steel paper grinding disc, high-speed grinding disc and grinding disc, is a disc-shaped coated abrasive tool made of steel paper as the base material and synthetic resin as the binder. It has high tensile strength and strong wear resistance. It can be installed on electric or pneumatic angle grinders to derust, deburr, paint and weld various surfaces of metal and non-metal materials. Ideal tools for grinding, smoothing, buffing in manufacturing and mechanical repair work, widely used in wood, furniture, shipbuilding, metallurgy, automobile, machinery, instrumentation, bridge and construction industries. [0003] At present, there are many researches and applications on steel paper sand discs at home and abroad, which are mainly r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B24D3/04B24D18/00B24D3/28
Inventor 王鹏王荣生
Owner JIANGSU FENGMANG COMPOUND MATERIAL SCI&TECH GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products