High gloss high abrasion resistance ultra-violet curing overprinting varnish of mobile phone and preparation method thereof

A high wear-resistant, varnish technology, applied in the field of varnish, can solve the problem of high price, achieve the effect of reducing friction coefficient, easy to implement, and increasing crosslinking density

Inactive Publication Date: 2011-02-09
苏州凯康化工科技有限公司
View PDF5 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, there are many types of mobile phone UV varnishes on the market. Since most of the raw materials are imported products, the price of the products produced is too high, and the final performance of domestic products Still can not meet the requirements of customers, so the development of low-cost high-performance mobile phone UV varnish has broad market prospects

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] A high-gloss and high-wear-resistant mobile phone UV varnish, which includes the following components in parts by weight:

[0047] Low viscosity polyester acrylate CN292 20 grams;

[0048] Hexafunctional aliphatic urethane acrylate CN9006 25 grams;

[0049] EO4PETA 20 g;

[0050] TMPTA 20 g;

[0051] TPGDA 15 grams;

[0052] HDDA 2 g;

[0053] 2-EHA 6 g;

[0054] BP 0.5 g;

[0055] 184 4 grams;

[0056] Reactive amine co-initiator CN381 1 gram;

[0057] BYK-020 1 g;

[0058] BYK-333 0.6 g;

[0059] 1.2 grams of solid wax powder;

[0060] 10 grams of ethyl acetate;

[0061] 5 grams of absolute alcohol;

[0062] The method for preparing the above-mentioned high-gloss and high-wear mobile phone UV varnish is as follows:

[0063]20 grams of low-viscosity polyester acrylate CN292, 25 grams of hexafunctional aliphatic urethane acrylate CN9006, 20 grams of EO4PETA, 20 grams of TMPTA, 15 grams of TPGDA, 2 grams of HDDA, 6 grams of 2-EHA, 0.5 grams of BP, 184 4 gra...

Embodiment 2

[0066] A high-gloss and high-wear-resistant mobile phone UV varnish, which includes the following components in parts by weight:

[0067] Low viscosity polyester acrylate CN292 25 grams;

[0068] Hexafunctional aliphatic urethane acrylate CN9006 20 grams;

[0069] EO4PETA 15 g;

[0070] TMPTA 10 g;

[0071] TPGDA 5 g;

[0072] HDDA 10 g;

[0073] 2-EHA 3 g;

[0074] BP 1.2 g;

[0075] 184 2 grams;

[0076] Reactive amine co-initiator CN381 2 grams;

[0077] BYK-020 0.2 g;

[0078] BYK-333 1 g;

[0079] Solid wax powder 2.0 grams;

[0080] 7 grams of ethyl acetate;

[0081] 15 grams of absolute alcohol;

[0082] The method for preparing the above-mentioned high-gloss and high-wear mobile phone UV varnish is as follows:

[0083] 25 grams of low-viscosity polyester acrylate CN292, 20 grams of hexafunctional aliphatic urethane acrylate CN9006, 15 grams of EO4PETA, 10 grams of TMPTA, 5 grams of TPGDA, 10 grams of HDDA, 3 grams of 2-EHA, 1.2 grams of BP, 184 2 gram, 2 ...

Embodiment 3

[0086] A high-gloss and high-wear-resistant mobile phone UV varnish, which includes the following components in parts by weight:

[0087] Low viscosity polyester acrylate CN292 30 grams;

[0088] Hexafunctional aliphatic urethane acrylate CN9006 15 grams;

[0089] EO4PETA 10 g;

[0090] TMPTA 15 g;

[0091] TPGDA 10 grams;

[0092] HDDA 6 grams;

[0093] 2-EHA 10 g;

[0094] BP 2 grams;

[0095] 184 6 grams;

[0096] Reactive amine co-initiator CN381 4 grams;

[0097] BYK-020 0.6 g;

[0098] BYK-333 0.2 g;

[0099] 0.5 grams of solid wax powder;

[0100] 4 grams of ethyl acetate;

[0101] 10 grams of absolute alcohol;

[0102] The method for preparing the above-mentioned high-gloss and high-wear mobile phone UV varnish is as follows:

[0103] Low-viscosity polyester acrylate CN292 30 grams, hexafunctional aliphatic urethane acrylate CN9006 15 grams, EO4PETA 10 grams, TMPTA 15 grams, TPGDA 10 grams, HDDA 6 grams, 2-EHA 10 grams, BP 2 grams, 184 6 gram, 4 grams of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
glossaaaaaaaaaa
glossaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high gloss high abrasion resistance ultra-violet (UV) curing overprinting varnish of mobile phone and a preparation method thereof. The method of the invention uses low-viscosity polyester acrylate and aliphatic polyurethane acrylate as base resin which combines with ethoxylated pentaerythritol tetraacrylate, Trimethylolpropane triacrylate, Tri(propylene glycol) diacrylate, 1,6-hexanediol diacrylate and 2-ethylhexyl acrylate which are used as active diluent, alcohol and ethyl acetate which are used as diluent, benzophenone and 1-hydroxycyclohexyl phenyl ketone which are used as photoinitiator, reactive amine coinitiator, defoaming agent, flatting agent, slip agent and other agents to mix evenly and prepare the UV overprinting varnish. The overprinting varnish of the invention adopts the special raw material formula and has good lustrousness, adhesive force and mechanical stability; as some polyfunctional resins and resins with special functional groups are added, the crosslink density of the UV varnish is increased in the curing process and the hardness of the product is up to 5-7H; and as solid wax powder used as the slip agent is added, the coefficients of friction can be reduced and the product can have extremely high wear resistance.

Description

technical field [0001] The invention relates to the field of varnishes, in particular to a layer of UV varnishes used on mobile phone casings. Background technique [0002] At present, there are many varieties of mobile phone UV varnishes on the market. Since most of the raw materials are imported products, the price of the products produced is too high, and the final domestic performance still cannot meet the requirements of customers. Therefore, low-cost high-performance mobile phones are developed. UV varnish has a broad market prospect. Contents of the invention [0003] The present invention is just to overcome the above-mentioned deficiencies, and the technical problem to be solved is to provide a high-gloss and high-wear-resistant mobile phone UV varnish with low price and excellent performance. [0004] The technical problem that the present invention also needs to solve is to provide the manufacture method of above-mentioned mobile phone UV varnish. [0005] In ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D167/06C09D175/14
Inventor 黄伊君
Owner 苏州凯康化工科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com