Method for processing novel environmental-protection spiral cable with high elasticity

A technology of a spiral cable and a processing method, applied in the cable field, can solve the problems of poor resilience, environmental pollution, and short service life of the spiral cable, and achieve the effects of convenient operation, good temperature resistance and low cost

Active Publication Date: 2011-04-20
ZHENJIANG HUAYIN INSTR & ELECTRICAL EQUIP
View PDF5 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The service life of the spiral cable processed by this method is relatively short, and the rebound performance is poor. Usually, after being stretched 500 times, the proper rebound performance of the spiral cable is lost, and the cable is completely straightened; in addition, the PVC material In the process of production and use, polybrominated biphenyls and polybrominated diphenyl ethers will be produced, which will pollute the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] A processing method of a novel environment-friendly high-elasticity spiral cable, the steps are as follows:

[0040] 1. Copper wire conductors are used for bundle twisting to make the inner core wire of the cable

[0041] 2、 Use TPU as raw material to process cables;

[0042] 2.1. Dry the TPU, the drying temperature is: 185°C; the time is: 5 hours; soften the TPU material; carry out plasticity;

[0043] 2.2. Coat the TPU processed in the above steps on the core wire through an extruder to form a cable;

[0044] The processing conditions of the extruder are: the temperature of the feeding section is: 160°C;

[0045] The temperature of the plasticizing section is: 85°C;

[0046] Head temperature: 185°C;

[0047] The core wire passes through the injection port of the extruder at a speed of 40 revolutions per minute;

[0048] The eye mold temperature is 185 degrees,

[0049] 3. Roll the cable into shape with a coiled rod;

[0050] 4. The rolled and shaped cable is...

Embodiment 2

[0054] A processing method of a novel environment-friendly high-elasticity spiral cable, the steps are as follows:

[0055] 1. Copper wire conductors are used for bundle twisting to make the inner core wire of the cable

[0056] 2、 Use TPU as raw material to process cables;

[0057] 2.1. Dry the TPU, the drying temperature is: 195°C; the time is: 3.5 hours; soften the TPU material; carry out plasticity;

[0058] 2.2. Coat the TPU processed in the above steps on the core wire through an extruder to form a cable;

[0059] The processing conditions of the extruder are: the temperature of the feeding section is: 170°C;

[0060] The temperature of the plasticizing section is: 155°C;

[0061] Head temperature: 190°C;

[0062] The core wire passes through the injection port of the extruder at a speed of 20-60 revolutions per minute;

[0063] Eye mold temperature is 190 degrees;

[0064] Eye mold: the cable extruded from the nozzle of the extruder;

[0065] 3. Roll the cable ...

Embodiment 3

[0070] A processing method of a novel environment-friendly high-elasticity spiral cable, the steps are as follows:

[0071] 1. Copper wire conductors are used for bundle twisting to make the inner core wire of the cable

[0072] 2、 Use TPU as raw material to process cables;

[0073] 2.1. Dry the TPU, the drying temperature is: 200°C; the time is: 3 hours;

[0074]2.2. Coat the TPU processed in the above steps on the core wire through an extruder to form a cable;

[0075] The processing conditions of the extruder are: the temperature of the feeding section is: 180 ℃;

[0076] The temperature of the plasticizing section is: 190°C;

[0077] The head temperature is: 195°C;

[0078] The core wire passes through the injection port of the extruder at a speed of 20 revolutions per minute;

[0079] Eye mold temperature is 195 degrees;

[0080] 3. Roll the cable into shape with a coiled rod;

[0081] 4. The rolled and shaped cable is shaped into a spiral cable through an oven a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a method for processing a novel environmental-protection spiral cable with high elasticity, which comprises the following steps of: 1, using a copper wire conductor to twist to make the internal core of the cable; 2, using TPU as raw material to process the cable; 3, rolling the cable wire with a reeling rod; 4, forming the reeled cable wire into a spiral cable by using a high temperature oven, wherein the temperature of the oven is 145 DEG C and the time is 20 minutes; and 5, cooling the formed spiral cable with cooling water to prepare the novel environmental-friendly spiral cable. The invention improves the temperature resistance and resillence of the product via improvement of the process.

Description

technical field [0001] The invention relates to a cable, in particular to a spiral cable and a processing method thereof, belonging to the technical field of cable processing. Background technique [0002] Spiral cable is a kind of equipment connection line that uses scalability to work. It is mainly used to control the electrical connection of the movement of movable equipment. It can rebound quickly in a short time. It is widely used in mobile equipment such as automobiles, machines, and instruments. . The spiral cable in the prior art includes a wire core and a sheath, and the sheath covers the outer periphery of the wire core. [0003] The processing method of traditional spiral cables usually uses oxide as a thermal initiator to add polyethylene, polyethylene is extruded onto the wire core at a low temperature at the decomposition temperature of the oxide, and then heated to a temperature above the decomposition temperature of polyethylene to form a cross-linking react...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): H01B13/008
Inventor 季忠银
Owner ZHENJIANG HUAYIN INSTR & ELECTRICAL EQUIP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap