Method for plating metal silver on textile fabric to form pattern through magnetron sputtering
A textile fabric, magnetron sputtering technology, applied in textile decoration, textile and papermaking, etc., can solve the problems of low production efficiency of chemical plating process, allergy or discomfort to pure silver, poor coating adhesion, etc., to overcome vacuum heat Evaporation process, clear silver coating pattern, good coating adhesion
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0017] Example 1 After fully dissolving gum arabic and water in a mass ratio of 70:100, use the designed screen pattern to print on the surface of the cotton cloth to form a colorless and transparent pattern shape; Under the condition of 17W, DC magnetron sputtering was carried out for 10 minutes to sputter metallic silver onto the surface of the textile fabric; after the sputtering was completed, the cotton cloth was rinsed in 40°C water for 20 minutes, and the gum arabic and the silver coated on the gum arabic were The silver was washed away, resulting in a silver-plated cotton cloth with a silver-plated pattern.
[0018] The specific performance of silver-plated cotton cloth is as follows:
[0019] 1. The color effect of cotton cloth after removing the matrix material:
[0020]
L *
a *
b *
C *
h
[0021] Swatch primary color
83.598
-0.174
0.45
0.482
111.139
silver plating color
...
Embodiment 2
[0034] Example 2 After fully dissolving gum arabic and water in a mass ratio of 70:100, use the designed screen pattern to print on the surface of the silk cloth to form a colorless and transparent pattern shape; then put the silk cloth under an argon pressure of 2Pa 1. Under the condition of power 17W, carry out DC magnetron sputtering for 10 minutes to sputter metallic silver onto the surface of silk cloth; The silver on the gum arabic was washed away, resulting in a silver-plated silk cloth with a silver-plated pattern.
[0035] The specific properties of silver-plated silk cloth are as follows:
[0036] 1. The color effect of silk cloth after removing the matrix material:
[0037]
L *
a *
b *
C *
h
Swatch primary color
81.496
-0.129
0.617
0.63
101.768
silver plating color
75.737
-0.156
7.233
7.235
91.235
[0038] The parameter values of two different ...
Embodiment 3
[0047]Example 3 After fully dissolving gum arabic and water in a mass ratio of 70:100, use the designed screen pattern to print on the surface of the polyester cloth to form a colorless and transparent pattern shape; then put the polyester cloth under an argon pressure of 2Pa 1. Under the condition of power 17W, carry out DC magnetron sputtering for 10 minutes, and sputter metallic silver onto the surface of the polyester cloth; The silver on the gum washes away, revealing the silver plated pattern on the polyester cloth.
[0048] The specific properties of silver-plated polyester cloth are as follows:
[0049] 1. The color effect of polyester cloth after removing the matrix material:
[0050]
L *
a *
b *
C *
h
Swatch primary color
82.68
4.078
-13.83
14.419
286.429
pattern color
81.6
3.96
-13.054
13.642
286.874
[0051] The parameter values of two differe...