Limonite purple-clay product and preparation method thereof

A technology of wood fish stone and products, which is applied to clay products, other household utensils, household utensils, etc. It can solve the problems of controlling the mixing ratio, extremely high requirements for calcination temperature, failure to disclose the preparation process, and great difficulty in firing, etc., to achieve The effect of light weight, high plasticity and high strength

Active Publication Date: 2013-04-17
北方红杉生态科技有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the above application puts forward new ideas for improving the plasticity and air permeability of Muyu stone products by using the leftovers of Muyu stone, it is extremely difficult to fire mixed products of Muyu stone and purple sand, especially in controlling the mixing ratio, calcination temperature, etc. extremely demanding
The inventors of the above patent applications did not make a substantial breakthrough in the two technical problems of mixing ratio and firing temperature, so these patent applications failed to disclose the specific preparation process, that is to say, they did not make specific products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Muyushi Zisha mouth cup is made of the following raw materials in weight percentage: 35% of Muyushi and 65% of Yixing red clay.

[0016] Preparation:

[0017] (1), the Muyu stone stone and the purple sand mud are respectively ground into 110 mesh powders for subsequent use;

[0018] (2), mix Muyu stone powder and purple clay powder in proportion, add water and stir to make mud tire;

[0019] (3), after the mud tire is sealed and packaged with a plastic film, it will be stale for 13 days and then it will be used for later use;

[0020] (4), the stale mud tires are made into blanks of required products, dried in the shade indoors for 3 days, and then the blanks dried in the shade are polished and polished to make semi-finished products;

[0021] (5) Put the semi-finished product into the kiln for firing, the kiln temperature is controlled at 1150° C. for 17 hours and then turn off the flame and cool down to obtain the desired product.

Embodiment 2

[0023] Muyushi Zisha Teapot is made of the following raw materials in weight percentage: 40% of Muyushi and 60% of Yixing Red Clay.

[0024] Preparation:

[0025] (1), the Muyu stone stone and the purple sand mud are respectively ground into 120 mesh powders for subsequent use;

[0026] (2), mix Muyu stone powder and purple clay powder in proportion, add water and stir to make mud tire;

[0027] (3), after the mud tire is sealed and packaged with a plastic film, it will be stale for 15 days and then it will be used for later use;

[0028] (4), making the blank of the required product from the stale mud tire, drying in the shade indoors for 2 days, then grinding and polishing the blank dried in the shade to make a semi-finished product;

[0029] (5) Put the finished semi-finished product into the kiln for firing, the kiln temperature is controlled at 1160° C. for 15 hours and then turn off the flame and cool down to obtain the desired product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a limonite purple-clay product, which consists of the following raw materials in percentage by weight: 30 to 50 percent of limonite, and 50 to 70 percent of purple-clay mud. The preparation method comprises the following steps: grinding the limonite and the purple clay mud into powder of between 80 and 120 meshes; mixing according to a proportion, adding water and stirringto prepare unfired pottery; sealing and packaging the unfired pottery, and aging for 10 to 15 days; preparing a blank of the required product, and drying in the shade indoors for 2 to 3 days; grinding and polishing the shady dried blank to prepare a semi-finished product; and firing the prepared semi-finished product in a kiln for 15 to 20 hours at the temperature of between 1,120 and 1,180 DEG C, and cooling to prepare the required product. In the invention, the limonite resource is sufficiently utilized, and waste is turned into wealth; and the fired limonite purple-clay product has light weight, high strength and no toxicity or radiation, the original characteristic and separated trace elements of the limonite have no changes, and the advantages of good ventilation and plasticity of the purple-clay are combined. The limonite purple-clay product can be manufactured into various nice new material tea sets, mugs and other products.

Description

Technical field [0001] The invention relates to the technical field of household utensils or table utensils, in particular to a wooden fish stone product containing purple sand and a preparation method thereof. Background technique [0002] The material properties of Muyu Stone and its health care functions have been known by more and more people. For example, making tea with wooden fish stone vessels can prolong the service life of the tea and have a better aroma; use wooden fish stone vessels to hold wine can reduce the methanol content and keep the alcohol content unchanged. For another example, because Muyu stone contains a variety of trace elements, the trace elements precipitated by using Muyu stone tea set to hold water can improve human metabolism and enzyme activity, promote blood circulation, and enhance immunity; especially these trace elements precipitated from Muyu stone Elements can inhibit the growth of tumors, so they have anti-cancer and anti-cancer effects...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B33/00
Inventor 马仁水
Owner 北方红杉生态科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com