Rubber for sneaker sole and preparation method thereof

A technology for shoe soles and sports shoes, which is applied in the direction of shoe soles, applications, footwear, etc. It can solve the problems of shoe sole wear, poor exhaust, large shrinkage, etc., achieve good wear resistance and folding resistance, and prevent the penetration of ozone , The effect of fatigue life improvement

Active Publication Date: 2011-05-18
ANTA CHINA
View PDF1 Cites 32 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Due to its special purpose, sports shoes require the sole rubber to have wear resistance, anti-slip performance, and good folding resistance. However, the rubber used in current sports shoes is mainly formulated with isobutylene containing active bromine. -Isoprene copolymer elastomer is the main material. This kind of rubber sole is very unstable in the production process. At the same time, due to the large shrinkage of this material, the sheet is not smooth, and the thickness of the sheet is not easy to control; the sole rubber is in In the later vulcanization process, due to the strong airtightness of the material, poor fluidity, and large shrinkage, factors such as color overflow are difficult to control, poor exhaust, etc., affect production efficiency and increase the defective rate
Although the sole rubber has a good performance in anti-slip performance, it has certain deficiencies in elasticity and wear resistance; the sole of the sports shoe is easy to slip during repeated bouncing and running, and the sole wears out quickly and loses its elasticity.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] A kind of rubber for sports shoe soles, comprising 3000g of butadiene rubber, 3000g of natural rubber, 1000g of isobutylene-isoprene copolymer elastomer containing 20% ​​active bromine by weight, 4000g of carboxylated nitrile rubber, 50g of tackifying resin, white Carbon black 7000g, tetrasulfide silane coupling agent 300g, polyethylene glycol 500g, di-tert-butyl-p-cresol 100g, paraffin 100g, paraffin-based rubber softening oil 200g, stearic acid 50g, zinc oxide powder 500g, sulfur 150g , and accelerator 210g, this accelerator is formed by mixing 111g of thiazoles, 66g of thiurams and 33g of dithiocarbamates.

[0047] The production technology of the rubber for sports shoe soles: polybutadiene, polyisoprene, isobutylene-isoprene copolymer elastomer containing 20% ​​active bromine by weight, carboxylated nitrile rubber, tackifying resin, White carbon black, tetrasulfide silane coupling agent, polyethylene glycol, di-tert-butyl p-cresol, paraffin, paraffin-based rubber so...

Embodiment 2

[0049] A kind of rubber for sports shoe soles, the preparation method is: with butadiene rubber 9590g, natural rubber 5480g, the isobutylene-isoprene copolymer elastomer that contains weight content 15% active bromine: 4110g, carboxylated nitrile rubber: 8220g, Tackifying resin 411g, white carbon black 8220g, tetrasulfide silane coupling agent 822g, polyethylene glycol 1096g, di-tert-butyl p-cresol 274g, paraffin wax 137g, paraffin-based rubber softening oil 548g, stearic acid 274g, zinc oxide powder is 822g, pour into the internal mixer for mixing, mixing time 7 minutes, temperature 120 ~ 140 ℃, after mixing evenly, discharging, discharging, cooling. Then put the cold and well-prepared material into the material preparation wheel and heat it, then add 400g of sulfur, the specific accelerators are: thiazoles: 80g, thiurams: 320g, dithiocarbamates: 100g, and knead , the time is 5 minutes, the temperature is 50-70 ℃, after mixing evenly, the sheet is produced to obtain 40904g of...

Embodiment 3

[0051]A kind of rubber for sports shoe soles, its preparation method is: with polybutadiene: 16170g, polyisoprene; 7700g, the isobutylene-isoprene copolymer elastomer of active bromine: 5775g, carboxylated nitrile rubber: 8855g, tackifying resin 578g, white carbon black 15400g, tetrasulfide silane coupling agent 1155g, polyethylene glycol 1540g, di-tert-butyl p-cresol 385g, paraffin 193g, paraffin-based rubber softening oil 770g, stearic acid 385g , Zinc oxide powder 1155g, pour into the internal mixer for mixing, mixing time 8 minutes, temperature 120 ~ 140 ℃, after mixing evenly, discharging, discharging, cooling. Then put the cold and well-prepared aniseed material into the material preparation wheel and heat it, add sulfur: 600g, accelerators: thiazoles: 120g, thiurams: 480g, dithiocarbamates: 150g, and mix. , the time is 4 minutes, the temperature is 50-70°C, after uniform mixing, the sheet is produced to obtain 61411g of super anti-slip and wear-resistant rubber material...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses rubber for a sneaker sole, and the rubber provided by the invention comprises the following components in parts by weight: 30-70 parts of butadiene rubber, 10-30 parts of natural rubber, 10-30 parts of bromobutyl rubber, 15-40 parts of carboxylated nitrile rubber, 2-5 parts of polyethylene glycol, 0.5-2 parts of stearic acid, 2-5 parts of zinc oxide, 1.5-2 parts of vulcanizer, 1.6-2.1 parts of accelerator, 0.5-2.0 parts of tackifier, 30-70 parts of white carbon black, 3-3.2 parts of coupling agent, 2-5 parts of softening oils, 1-3 parts of anti-aging agent and 0.5-1 part of paraffin. The invention further discloses a preparation method of the rubber. The rubber for the sneaker sole, provided by the invention, has incomparable slip prevention performance compared with the ordinary rubber shoe sole, and has multiple functions such as excellent wear resistance, bend resistance, and the like.

Description

technical field [0001] The invention relates to rubber for sports shoe soles, especially rubber for sports shoe soles, and a preparation method thereof. Background technique [0002] Due to its special purpose, sports shoes require the sole rubber to have wear resistance, anti-slip performance, and good folding resistance. However, the rubber used in current sports shoes is mainly formulated with isobutylene containing active bromine. -Isoprene copolymer elastomer is the main material. This kind of rubber sole is very unstable in the production process. At the same time, due to the large shrinkage of this material, the sheet is not smooth, and the thickness of the sheet is not easy to control; the sole rubber is in In the later vulcanization process, due to the strong air tightness, poor fluidity and large shrinkage of the material, factors such as color overflow are difficult to control, poor exhaust, etc., affect production efficiency and increase the defective rate. Alth...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L9/00C08L7/00C08L15/02C08L13/00C08L71/08C08K13/02C08K3/22C08K3/36A43B13/04
Inventor 柯育发成升良张奇隆何正清
Owner ANTA CHINA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com