Releasing agent and preparation method thereof

A release agent, weight percentage technology, used in manufacturing tools, casting equipment, metal processing equipment, etc., can solve problems such as unsatisfactory release effect, poor product qualification rate and forming quality, and improve product forming qualifications. rate, improve surface quality, and improve the effect of product forming rate

Active Publication Date: 2014-08-27
BEIJING ZHONG KE SAN HUAN HI TECH
View PDF8 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The disclosed mold release agent is mainly designed for the adhesion problem in the forming process of non-magnetic materials, and the demoulding effect for products of different shapes (especially for ring products with a large aspect ratio) is very unsatisfactory. The qualified rate and forming quality are poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Releasing agent and preparation method thereof
  • Releasing agent and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A release agent used in the forming process of magnetic materials, which consists of the following components: graphite powder with a weight percentage of 0.1, fatty acid derivatives with a weight percentage of 0.1, paraffin wax with a weight percentage of 0.1, and dodecane with a weight percentage of 0.1 A mixture of sodium alkylbenzene sulfonate, 0.1 weight percent glyceride, and 99.5 weight percent gasoline. The mixture mixed according to the above ratio is heated to a temperature of 60-100° C., mixed and dissolved for 30-45 minutes, and the mold release agent in the forming process of the magnetic material is obtained.

Embodiment 2

[0020] A release agent used in the forming process of magnetic materials is composed of the following components: graphite powder with a weight percentage of 2, fatty acid derivatives with a weight percentage of 5, paraffin wax with a weight percentage of 2, and dodecane with a weight percentage of 0.5 A mixture of sodium alkylbenzene sulfonate, 2.5% by weight glyceride, and 88% by weight gasoline. The mixture mixed according to the above ratio is heated to a temperature of 60-100° C., mixed and dissolved for 30-45 minutes, and the mold release agent in the forming process of the magnetic material is obtained.

Embodiment 3

[0022] A release agent used in the forming process of magnetic materials is composed of the following components: graphite powder with a weight percentage of 1, fatty acid derivatives with a weight percentage of 3, paraffin wax with a weight percentage of 1, and dodecane with a weight percentage of 0.3 A mixture of sodium alkylbenzene sulfonate, 1.5 weight percent glyceride, and 93.2 weight percent gasoline. The mixture mixed according to the above ratio is heated to a temperature of 60-100° C., mixed and dissolved for 30-45 minutes, and the mold release agent in the forming process of the magnetic material is obtained.

[0023] The composition of the components of each of the above examples is shown in Table 1 below. In addition, see Table 2 for the product technical parameters of the various embodiments.

[0024] Table 1

[0025]

[0026] Table 2

[0027]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a releasing agent used in a process of forming a magnetic material, which comprises the following components: 0.1-2 percent by weight of graphite powder, 0.1-5 percent by weight of fatty acid derivative, 0.1-2 percent by weight of paraffin, 0.1-0.5 percent by weight of sodium dodecyl benzene sulfonate, 0.1-2.5 percent by weight of glyceride and 88-99.5 percent by weight of gasoline mixture. The invention also discloses a preparation method of the releasing agent. According to the releasing agent provided by the invention, the problem of adhesion in the process of forming the magnetic material is solved, and the surface quality of a permanent magnet material casting is improved, especially the annular permanent magnet material product with large long diameter ration; and by using the releasing agent, the surface roughness of the permanent magnet material blank product is reduced, and the forming qualified rate of products is improved.

Description

technical field [0001] The invention relates to a release agent used in the forming process of magnetic materials and a preparation method thereof. Background technique [0002] The mold release agent is a kind of isolation film applied between the product and the mold to prevent the formed metal material product from sticking to the mold, so that the product can be easily released from the mold, while ensuring the surface quality of the product and the mold are intact. [0003] Common die-casting release agents in the prior art include oil-based release agents, water-based release agents and powder release agents: [0004] Chinese invention patent application No. 200610024658.1 discloses an oil-based magnetic material release agent and its preparation method; [0005] Chinese invention patent application No.200410086761.X discloses a water-based metal mold release agent; [0006] Chinese invention patent application No. 200710051860.8 discloses a powder release agent for ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22C3/00
Inventor 陈国安王浩颉王湛钮萼李正饶晓雷胡伯平
Owner BEIJING ZHONG KE SAN HUAN HI TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com