Environmentally-friendly interior and exterior wall coating and preparation method and construction method thereof

An environmentally friendly technology for interior and exterior walls, applied in coatings, buildings, building structures, etc., can solve the problems of waste of useful substances in acrylic sheets, environmental pollution, etc., and achieve the effects of less raw material varieties, simple construction technology, and reduced raw material costs

Active Publication Date: 2011-06-22
ZHUHAI SHENGXIYUAN MECHANICAL & ELECTRICAL EQUIP CO LTD
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, it is treated as garbage, which not only pollutes the environment but also wastes the useful substances in the acrylic sheet

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] A) The coating formula is as follows:

[0049] Waste polyvinyl alcohol, 10% (mass) aqueous solution, 50 mass parts,

[0050] Waste rock powder, 80-120 mesh, 25 parts by mass,

[0051] Borax, 1% (mass) borax aqueous solution 2 mass parts,

[0052] Antifungal agent, P803 0.05 parts by mass,

[0053] B) specific operation

[0054] ① Prepare 10% (mass) polyvinyl alcohol aqueous solution

[0055] Weigh 10Kg of waste polyvinyl alcohol and 90Kg of water according to the amount required to prepare a 10% (mass) polyvinyl alcohol aqueous solution, first heat the water to 75°C, then add waste polyvinyl alcohol to the water, and stir until the All dissolved, can be stored for later use;

[0056] ② Prepare 1% (mass) borax aqueous solution

[0057] Weigh 1Kg of borax and 99Kg of water according to the amount required to prepare a 1% (mass) borax aqueous solution, first heat the water to 65°C, then add borax to the water, stir until the borax is completely dissolved, and then sa...

Embodiment 2

[0063] A) The coating formula is as follows:

[0064] Waste polyvinyl alcohol, 12% (mass) aqueous solution, 60 mass parts,

[0065] Waste rock powder, 80-120 mesh, 35 parts by mass,

[0066] Boric acid, 3 parts by mass of 1% (mass) boric acid aqueous solution,

[0067] Antifungal agent, P803 0.05 parts by mass,

[0068] B) specific operation

[0069] ① Prepare 12% (mass) polyvinyl alcohol aqueous solution

[0070] Weigh 12Kg of waste polyvinyl alcohol and 88Kg of water according to the amount required to prepare a 12% (mass) polyvinyl alcohol aqueous solution, first heat the water to 80°C, then add the waste polyvinyl alcohol to the water, stir until the All dissolved, can be stored for later use;

[0071] ② Prepare 1% (mass) boric acid aqueous solution

[0072] Weigh 1Kg of boric acid and 99Kg of water according to the amount required to prepare a 1% (mass) boric acid aqueous solution, first heat the water to 60°C, then add borax to the water, stir until the boric acid ...

Embodiment 3

[0078] A) The coating formula is as follows:

[0079] Industrial grade polyvinyl alcohol 1788, 16% (mass) aqueous solution, 80 parts by mass,

[0080] Waste rock powder, 80-120 mesh, 40 parts by mass,

[0081] Borax, 2.5% (mass) borax aqueous solution 3 mass parts,

[0082] Antifungal agent, P803 0.05 parts by mass,

[0083] B) specific operation

[0084] ① Prepare 16% (mass) polyvinyl alcohol aqueous solution

[0085] Weigh 16Kg of industrial grade polyvinyl alcohol 1788 and 84Kg of water according to the amount required to prepare a 16% (mass) polyvinyl alcohol aqueous solution, first heat the water to 92°C, then add industrial grade polyvinyl alcohol 1788 to the water, stir Until the polyvinyl alcohol is completely dissolved, it can be preserved for subsequent use;

[0086] ② Prepare 2.5% (mass) borax aqueous solution

[0087] Weigh 2.5Kg of borax and 97.5Kg of water according to the amount required to prepare a 2.5% (mass) borax aqueous solution, first heat the water...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to an environmentally-friendly interior and exterior wall coating and a preparation method and a construction method thereof. The coating is prepared from the following raw materials in part by mass: 40-80 parts of aqueous solution of polyvinyl alcohol with concentration of 8-10 percent (mass), 20-40 parts of 80-120 mesh waste stone dust, 1-8 parts of aqueous solution of boride with concentration of1-3 percent (mass) and 0.05 part of mildew preventive P803. The waste stone dust is obtained by grinding and screening a waste acrylic plate. Major ingredients of the waste acrylic plate include polymethyl methacrylate, aluminum hydroxide and calcium carbonate. The preparation method is simple. During construction, the coating is coated twice, and then a borax aqueous solution with concentration of 1-3 percent (mass) is sprayed.

Description

technical field [0001] The present invention relates to an environment-friendly interior and exterior wall coating and its preparation method and construction method, more specifically, relates to an environment-friendly interior and exterior wall coating using waste materials from the production of acrylic plates as main raw materials, its preparation method and construction method. Background technique [0002] Acrylic sheet is a commonly used architectural decorative sheet, and its main components are polymethyl methacrylate, aluminum hydroxide, and calcium carbonate. Enterprises that produce acrylic sheets often generate a lot of waste, including discarded acrylic sheets. At present, it is treated as garbage, which not only pollutes the environment but also wastes useful substances in the acrylic sheet. Contents of the invention [0003] The first object of the present invention is to provide an environmentally friendly interior and exterior wall coating that can redu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D129/04C09D133/12C09D7/12E04F21/06
Inventor 侯文顺胡英杰刘日鑫
Owner ZHUHAI SHENGXIYUAN MECHANICAL & ELECTRICAL EQUIP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka