High-strength nickel-chromium-silicon-copper alloy material and processing technology thereof

A technology of silicon-copper alloy and processing technology, which is applied in the field of high-strength nickel-chromium-silicon-copper alloy material and its processing technology, to achieve the effects of environmental protection, low cost and low toxicity

Active Publication Date: 2013-04-24
SHENYANG XINGGONG COPPER IND
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this alloy has the following disadvantages: beryllium is highly toxic, and as long as there is one milligram of beryllium dust in every cubic meter of air, people will be infected with acute pneumonia-beryllium lung disease; beryllium and cobalt metals are expensive, so that The material cost of beryllium cobalt zirconium copper alloy is relatively high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength nickel-chromium-silicon-copper alloy material and processing technology thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Example 1: Ni: 2.9%, Cr: 0.55%, Si: 0.7%, the total amount of impurities ≤ 0.3%, and the balance of Cu.

Embodiment 2

[0030] Example 2: Ni: 2.5%, Cr: 0.5%, Si: 0.5%, the total amount of impurities ≤ 0.3%, and the balance of Cu.

Embodiment 3

[0031] Embodiment 3: Ni: 2.1%, Cr: 0.7%, Si: 0.3%, the total amount of impurities ≤ 0.3%, and the balance of Cu.

[0032] Nickel can improve the mechanical properties and corrosion resistance of copper alloy materials, and has good electrical conductivity. Nickel and silicon can form a compound Ni 2 Si is soluble in copper; chromium, similar to nickel, can form chromium silicide, a compound soluble in solid copper with silicon, to strengthen the body; chromium is not easy to reduce the conductivity of copper, and can improve the mechanical properties of the material by precipitation hardening.

[0033] The embodiment of processing technology of the present invention is as follows:

[0034] Embodiment 1 (forged bar, specification 45*60*L):

[0035] 1. Casting

[0036] It adopts the semi-continuous casting method of industrial frequency electric furnace melting. Cu and Ni can be directly added into the furnace during melting and casting. Cr is pre-loaded into the copper tube i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a copper alloy material and a processing technology thereof, in particular to a high-strength nickel-chromium-silicon-copper alloy material and a processing technology thereof. The alloy material has low toxicity and low cost. The alloy material comprises the following components by mass: 2.1-2.9% of Ni, 0.4-0.7% of Cr, 0.3-0.7% of Si, not more than 0.3% of total impurities and the balance of Cu. The processing technology comprises the steps of casting, press processing, high-temperature solution hardening and heat treatment, cold press processing, aging heat treatment and mechanical processing.

Description

Technical field: [0001] The invention relates to a copper alloy material and its processing technology, more specifically, to a high-strength nickel-chromium-silicon-copper alloy material and its processing technology. Background technique: [0002] At present, in order to improve the unbalanced operation capacity of the turbo-generator and ensure the safety and reliability of the unit after the temperature rise caused by the negative-sequence current of the generator, the large-scale generator manufacturers in my country must have certain requirements for the selected rotor wedge material. High electrical conductivity and high mechanical properties at room temperature and high temperature. [0003] For many years, most of the turbogenerator rotor slot wedge materials used by some large-scale turbogenerator unit manufacturers in China have adopted the alloy material proposed by the Westinghouse Power Generation Company in the technical conditions of the United States, that i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C9/06C22F1/08B22D11/108B22D21/02
Inventor 白继明杨素娟王嗣杰李廷元
Owner SHENYANG XINGGONG COPPER IND